Table 1.
Criteria evaluated in confocal laser scanning microscopy.
Table 2.
Microtensile strength values, in MPa, 24 hours after adhesion, of the different types of treatments used in dentin (normal or eroded), and occurrence of premature failure of the specimens.
Table 3.
Microtensile strength values, in MPa, 8 months after adhesion, of the different types of treatments used in dentin (normal or eroded), and occurrence of premature failure of the specimens.
Fig 1.
Scanning electron microscopy analysis of the different groups in sound and eroded dentin, 24 hours after the adhesive process.
(A) Representative specimen of the control group–sound dentin. Underlying dentin without exposure of the dentinal tubules (asterisk). (B) Representative specimen of the control group–eroded dentin, where it is possible to observe a greater bonding of the cement to the eroded substrate (asterisks). (C) Representative specimen 2% chlorhexidine sound dentin, it is to observe the presence of the resin cement (asterisks) on the smear layer (arrow). (D) Representative specimen 2% chlorhexidine eroded dentin, there is a remarkable exposure of the dentinal tubules compared to sound dentin (arrows). (E) Representative specimen 20% polyacrylic acid sound dentin, presence of the dentinal tubules partially occluded by the smear plug (arrows). (F) Representative specimen 20% polyacrylic acid eroded dentin, evidencing the presence of cement on the dentin (asterisks). (G) Representative specimen 0.1 M EDTA–sound dentin, it is noted that both the smear layer and the smear plug were removed, with great exposure of the dentinal tubules (arrows). (H) Representative specimen 0.1 M EDTA–eroded dentin, the presence of cement on the left with adjacent smear layer (asterisks), and evident increase in the opening of the dentinal tubules in the regions of exposed dentin (arrows), compared to the sound dentin of the same group. Magnification 1000x.
Fig 2.
Scanning electron microscopy analysis of the different groups in sound and eroded dentin, 8 months after the adhesive process.
(A) Control group–sound dentin. Few or no presence of cement on the dentin, without exposure of the dentinal tubules (asterisks). (B) Control group–eroded dentin, showing the presence of mixed failure, with smear layer areas (asterisks) surrounded by resin cement (arrows). (C) 2% Chlorhexidine group–sound dentin. Presence of the resin cement on the dentin surface (asterisks), without exposure of the dentinal tubules. (D) 2% Chlorhexidine group–eroded dentin. Presence of the resin cement on the dentin surface (asterisks), whit few exposure of the dentinal tubules (arrows). (E) 20% Polyacrylic acid group–sound dentin. Few exposure of the dentinal tubules (asterisks). (F) 20% Polyacrylic acid group–eroded dentin. It is evidenced the presence of resinous material on the smear layer (asterisks) and many dentinal tubules exposed on the surface, with exposure of the collagen fibers (arrows); most of the exposed tubules are obliterated. (G) 0.1 M EDTA group–sound dentin, evidencing the presence of resin cement (asterisks), with few exposure of the dentinal tubules (arrow). (H) 0.1 M EDTA group–eroded dentin, evidencing the presence of a few exposed tubules on the surface and others filled by the resin cement (asterisks). Magnification 1000x.
Fig 3.
Incidence (%) of failures mode among treatment groups, 24 hours after the adhesion process.
Fig 4.
Incidence (%) of failures mode among treatment groups, 8 months after the adhesion process.
Fig 5.
Analysis in confocal microscopy of sound and eroded dentin submitted to different surface treatments.
(A) Control group–sound dentin. It is possible to observe a continuous interface, without cracks (asterisks) and without the formation of tags. (B) Control group–eroded dentin. Adhesive interface without hydrid layer formation, however, an intense formation of resin tags (arrows) was observed in relation to the sound dentin. (C) 2% Chlorhexidine group–sound dentin. Note the absence of cracks in the adhesive interface as well as hybrid layer formation (asterisks). (D) 2% Chlorhexidine group–eroded dentin. Absence of cracks in the adhesive interface, with formation of some visible tags (arrows). (E) 20% Polyacrylic acid group–sound dentin. Pronounced hybrid layer formation throughout the adhesive interface (asterisks). (F) 20% Polyacrylic acid group–eroded dentin. Hybrid layer formation throughout the adhesive interface, with increased thickness compared to sound dentin (asterisks) and tag formation ≤ 3 μm in almost all interface (arrows). (G) 0.1 M EDTA group–sound dentin. Regarding the quality of the adhesive interface, it is possible to note the absence of cracks, with the formation of some resin tags measuring from 9 to 15 μm (arrows). (H) 0.1 M EDTA group–eroded dentin. Absence of cracks in the adhesive interface, without hybrid layer, but with the very dense formation of resin tags as well as in depth. *d = dentin / *rc = resin cement. Asterisks: hybrid layer formation; arrows: resin tags formation.
Table 4.
Qualitative (scores) in confocal microscopy.