Applications involving biomolecules, such as enzymes, antibodies, and other proteins as well as whole cells, are often hampered by their unstable nature at extremely high temperature and in organic solvents.
We constructed enzyme-NPG biocomposites by assembling various enzymes onto the surface of nanoporous gold (NPG), which showed much enhanced biocatalytic performance and stability. Various enzymes with different molecular sizes were successfully tethered onto NPG, and the loadings were 3.6, 3.1 and 0.8 mg g−1 for lipase, catalase and horseradish peroxidase, respectively. The enzyme-NPG biocomposites exhibited remarkable catalytic activities which were fully comparable to those of free enzymes. They also presented enhanced stability, with 74, 78 and 53% of enzymatic activity retained after 20 successive batch reactions. Moreover, these novel biocomposites possessed significantly enhanced reaction durability under various thermal and in organic solvent systems. In a sample transesterification reaction, a high conversion rate was readily achieved by using the lipase-NPG biocomposite.
Citation: Wang X, Liu X, Yan X, Zhao P, Ding Y, Xu P (2011) Enzyme-Nanoporous Gold Biocomposite: Excellent Biocatalyst with Improved Biocatalytic Performance and Stability. PLoS ONE 6(9): e24207. https://doi.org/10.1371/journal.pone.0024207
Editor: Jian R. Lu, The University of Manchester, United Kingdom
Received: April 19, 2011; Accepted: August 2, 2011; Published: September 2, 2011
Copyright: © 2011 Wang et al. This is an open-access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.
Funding: This work was supported by grants from National Natural Science Foundation of China (20706035), New Teacher Foundation of Ministry of Education of China (20090131120005), and Excellent Middle-Aged and Youth Scientist Award Foundation of Shandong Province (BS2010SW016). Y. Ding is a Tai-Shan scholar supported by Independent Innovation Foundation of Shandong University and Shandong Natural Science Fund for Distinguished Young Scholars. The funders had no role in study design, data collection and analysis, decision to publish, or preparation of the manuscript.
Competing interests: The authors have declared that no competing interests exist.
The encapsulation of biomolecules, such as enzymes, antibodies, and other proteins as well as whole cells, on porous materials is an important approach to stabilize the biological components in what is often an unnatural environment while retaining their functions and activities –. However, there still exist a series of technical bottlenecks for practical applications of immobilized enzymes, such as low catalytic activity, restricted mass transfer, enzyme leaching upon reuse, and sophisticated and expensive synthesis procedures. Taking into consideration all these factors, nanoporous gold (NPG), fabricated by a simple dealloying method, was selected here as a support for enzyme immobilization due to its unique physicochemical properties –. NPG has tunable pores at a nanometer scale that could fit proteins with different molecular weights and dimensions and offer the possibility of adsorbing or entrapping biomolecules within the pores as well as on the external surfaces depending on the nature of the proteins. In addition, NPG is intrinsically a nanostructured bulk material, thus it can be easily employed and recovered for reuse. Moreover, NPG has a biocompatible and active surface, which offers the opportunity for covalent binding through for example the well known thiol-based self-assembled monolayer technology .
Materials and Methods
4-Nitrophenyl palmitate, p-nitrophenol, pyrogallol, lipase (Aldrich 534641 from Pseudomonas cepacia), catalase, and horseradish peroxidase (HRP) were purchased from Sigma-Aldrich (St. Louis, USA).
Nanoporous gold was made by chemically dealloying AgAu alloy foils (Ag78Au22 at.%, 25 µm in thickness, purchased from Changshu Noble Metal Company, China) in concentrated HNO3 at room temperature for a certain period of time . The size and specific surface are ca. 35 nm and ca. 14 m2 g−1, respectively. For enzyme immobilization on NPG, 1 ml of enzymes solution (1.0 mg ml−1 of lipase, 1.0 mg ml−1 of catalase, and 0.01 mg ml−1 of HRP, respectively) was mixed with 18 mg NPG. Then the mixture was incubated at 4°C. After incubation, the supernatant was removed by centrifugation (5,000× g for 5 min), and the enzyme-NPG biocomposite was washed five times with distilled water before measuring the activity of the immobilized enzyme. The amount of immobilized enzyme was determined by Bradford protein assays .
The activity of immobilized or free lipase was determined by measuring its initial hydrolysis rate of 4-nitrophenyl palmitate at 40°C according to a previous literature . One unit (U) of lipase activity is defined as the amount of lipase which catalyzes the production of 1 µg p-nitrophenol under the experimental conditions. For determining HRP activity, we inserted the biocomposite in a medium containing pyrogallol at 5% (w/v) and hydrogen peroxide at 0.5 (w/v), while absorbance at 420 nm was monitored with time, as described elsewhere . The activity of catalase was determined spectrophotometrically by indirect measurement according to a previous literature . The enzymatic reaction was carried out at 25°C, then stopped with 2.7 ml of 50 mM ammonium molybdate and the yellow complex of molybdate and hydrogen peroxide was measured at 405 nm.
The microstructures of NPG and NPG bound to lipase were characterized using a JEOL JSM-6700F field emission scanning electron microscope (SEM), equipped with an Oxford INCA x-sight energy-dispersive X-ray spectrometer for compositional analysis. X-ray photoelectron spectroscopy (XPS) was taken with ESCALAB 250 (Thermo-Fisher Scientific, UK), using monochromated Al Kα excitation at pass energy of 150 eV for survey spectra and 20 eV for core lever spectra. The bonding energies were referenced to the C 1s BE at 284.6 eV. Lipase-loaded NPG and bare NPG were stained with a solution of fluprescein isothiocyanate dextran in carbonate buffer (0.5 mol l−1, pH 8.0) for 30 min at 30°C, and then washed with distilled water. After staining, the samples were characterized using an Eclipse 80i/90i Microscope (Nikon, Japan). The surface area of NPG used was measured with Quadrasorb SI-MP (Quantachrome Instrument) using the BET method.
Thermal and organic solvent stabilities
The thermal stability of the lipase-NPG biocomposite was examined by measuring the residual activity at 40°C after incubation in Tris-HCl buffer (50 mM, pH 8.0) for 30 min at 50, 60, and 70°C. To test their durability toward organic media, free and lipase-NPG biocomposite samples were exposed to an aqueous solution containing 50% (v/v) benzene, ethyl acetate, and chloroform, at 30°C for 12 h on a rotary shaker at 150 rpm. And then the residual activity was detected.
Enzymatic transesterification reaction
The transesterification reaction was carried out in 100-ml flasks at 40°C on a rotary shaker at 150 rpm. The composition of the reaction mixtures was 2.0 ml of refined soybean oil, immobilized lipase (2.7 mg of lipase) or free lipase (2.7 mg), 1.0 ml distilled water and 167 µl of methanol (added twice, the final volume ratio of oil∶methanol is 6∶1). After 24 h reaction, the methyl esters were extracted in n-hexane for gas chromatographic analysis .
Construction of enzyme-NPG biocomposite
To investigate the potential of NPG for bio-macromolecule immobilization, several model enzymes such as lipase, catalase and HRP with different molecular weights were employed in this study. The dimensions of lipase, catalase and HRP revealed by their crystal structures as reported are in the range of 4–10 nm as shown in Table 1 –. According to theoretical calculations, maximum stabilization of a protein can be achieved by adsorption within spherical cages whose diameter is 2–6 times of the dimension of the native molecule . Therefore, NPG with a pore size of ca. 35 nm was used here for enzyme immobilization. The procedure of the enzyme adsorption onto NPG can be illustrated in Figure 1.
Characterization of enzyme-NPG biocomposite
Samples of NPG before and after the enzyme loading were characterized using scanning electron microscopy. Compared with the bare NPG (Figure 2a), the enzyme-NPG biocomposite looks a little blurred due to its poorer conductivity (Figure 2b). Smaller pore sizes and relatively smoother surface morphology were found for the enzyme-NPG biocomposite, indicating preferential immobilization of the enzyme molecules over the ligament site with high radial curvatures. A similar phenomenon was observed previously when modifying the NPG surface with Pt . Meanwhile, a homogeneous fluorescence distribution on the enzyme-NPG biocomposite was observed after staining with fluorescein isothiocyanate dextran by fluorescence microscopy analysis (inset in Figure 2b), while no fluorescence was observed on the bare NPG treated under the same conditions (inset in Figure 2a). The loadings of lipase, catalase and HRP are 3.6, 3.1 and 0.8 mg g−1, respectively (Table 1). For HRP, the lower loading may be due to the lower enzyme concentration.
Catalytic performance of enzyme-NPG biocomposite
As expected, the enzyme-NPG biocomposites demonstrated remarkable catalytic performance and stability. There were nearly no decreases in catalytic activities upon immobilization for the enzyme-NPG biocomposites as shown in Figure 3a. These results indicated significant improvement of catalytic activities in our systems as compared with the less biocompatible ones –. This should be associated with NPG's excellent biocompatibility, active surface, and high conductivity, which are very important for enzyme immobilization. In addition, the enzyme-NPG biocomposites exhibited remarkable reaction stability (Figure 3b). For example, no decrease in activity was observed by the lipase-NPG biocomposite after recycling for ten times (Figure 3b). Moreover, there is still 74% of activity after 20 successive batch reactions. While for the catalase-NPG and HRP-NPG biocomposites, their activities decreased by only ca. 7 and 23% after ten cycles, respectively. After 20 successive batch reactions, the catalase-NPG and HRP-NPG biocomposites could still maintain 78 and 53% of activities, respectively.
Stability of lipase-NPG biocomposite under different conditions
The stability of the lipase-NPG biocomposite under various thermal and in organic solvent systems was investigated. The logarithm of the partition coefficient between 1-octanol and water (log P) is widely used to characterize molecular lipophilicity and hydrophobicity . In order to study the tolerance of the lipase-NPG biocomposite to organic solvents, benzene (log P is 2.0), ethyl acetate (log P is 0.68), and chloroform (log P is 2.0) were employed. As shown in Figure 4a, for free lipase, only 50, 27, and 42% of initial activity were observed after treatment with benzene, ethyl acetate, and chloroform, respectively. In contrast, the lipase-NPG biocomposite exhibited much enhanced stability in organic solvents with 86, 81, and 85% of activity retention after treatment in the same solvents. No significant decrease in catalytic activity was observed for the lipase-NPG biocomposite after 10 cycles under the test conditions (Figure 4b). Even after 20 recycles, there were sill 47, 33 and 38% activity retention for the lipase-NPG biocomposite treated by benzene, ethyl acetate, and chloroform, respectively.
The risk of denaturation caused by heat could be effectively alleviated by using the lipase-NPG biocomposite as shown in Figure 5. After incubation in the temperature range from 50 to 70°C for 30 min, only 62, 59, and 54% of initial activity were observed for free lipase (Figure 5a). Compared with free lipase, the lipase-NPG biocomposite presented evidently higher stability and better reusability. After treated by heat, the lipase-NPG biocomposite exhibited much enhanced stability with 75, 74, and 76% of activity retention for 50, 60 and 70°C, respectively. In addition, almost no decrease in catalytic activity was observed after 10 cycles for the lipase-NPG biocomposite upon pre-treatments by heat. After 20 cycles, 61, 62, and 40% of activity remained for the lipase-NPG biocomposite incubated at 50, 60, and 70°C, respectively (Figure 5b).
In order to further demonstrate the excellent performance of the lipase-NPG biocomposite, transesterification reaction for biodiesel production was investigated. The conversion of soybean oil to biodiesel by free lipase was 74% at 24 h, while the lipase-NPG biocomposite displayed even higher activity and superior stability in this reaction as shown in Figure 6. During the first two cycles, the conversion rate maintained an impressive high value of more than 90%. After 10 cycles, the conversion rate was still over 68%.
The aim of enzyme immobilization is to maintain the catalytic activity whilst improving its stability and ease of reuse. In this study, we constructed the enzyme-NPG biocomposites by assembling various enzymes onto the surface of NPG. It was clearly observed that the resulted enzyme-NPG biocomposites demonstrated not only remarkable catalytic performance but also excellent reuse stability compared with free enzymes. These results are superior to those reported in literatures , , .
Excellent catalytic performance alone is not enough to ensure a high stability under different conditions. The stability of enzyme plays a key role during the practical use of enzyme. From above results, the enzyme-NPG biocomposites have presented remarkable catalytic performance. Lipase is one of the most utilized classes of biocatalysts , . It can be widely used in the enzymatic organic synthesis and clinical analysis . Denaturation of lipase, which destroys its catalytic activity and stability, can be induced by heat or organic solvents. Thus, the lipase-NPG biocomposite was investigated under different experimental conditions. The results showed that the novel biocomposite possessed significantly enhanced reaction durability under various thermal and in organic solvent systems. In addition, a conservative estimation suggested that the lipase-NPG biocomposite could retain its high activity for at least 240 h in transesterification reaction system. These results were markedly better than previous reports where a significant decrease in activity was observed within 10 recycles in biodiesel production using immobilized lipase , –. The high conversion rate once again confirmed that NPG is an excellent support for enzyme immobilization.
The above results clearly suggested that the immobilization using bio-compatible and highly conductive NPG could enhance the stability of enzymes. The excellent catalytic performance and stability of the enzyme-NPG biocomposites might be explained by their physical confinement inside the relatively small pores , , . Especially, the size match between pore dimension and the molecular diameter of enzymes and the suitability of gold to function as an immobilization medium are of key importance in achieving high enzymatic stability , . This involves the adsorption of the enzyme with its active site oriented away from the porous surface with little leaching yet sufficient mobility to retain catalytic activity , , , . Moreover, it is well accepted that the interaction of nanoscale gold with NH2 was as strong as that with the commonly used SH , . The lipase from Pseudomonas cepacia has fourteen lysine residues and six cysteine residues (data from http://web.expasy.org/protparam/). The covalent attachments of enzymes by the amino and mercapto groups onto the surface of NPG could prevent the enzyme leaching, and the curvatures of the porous surfaces could provide an ideal configuration for multipoint covalent attachments to global enzyme molecules, resulting in better operational stability . To prove this, X-ray photoelectron spectroscopy was used to probe the chemical state of the surface for the lipase-NPG biocomposite. In free lipase, there is only a single broad peak at about 163.7 eV for S2p (Figure 7a). In contrast, after immobilization on NPG, it splits into two peaks with binding energy in the range from 162.0 to 165.0 eV corresponding to the chemical states of sulfur in Au-S and S-H, respectively . Additionally, the N1s binding energy of nitrogen in protein at 399.6 eV was also observed in the lipase-NPG biocomposite as shown in Figure 7b, while no the signal of N1s was observed on the bare NPG. These results consist with other researchers' reports when lactate dehydrogenase encapsulated in poly nanofibers and fluorescein isothiocyanate-conjugated bovine serum albumin encapsulated in poly(ethylene glycol) and poly(ε-caprolactone) , . These features make NPG an efficient support for chemical and biomolecular species.
In conclusion, a simple and efficient method for enzyme immobilization onto a nanoporous metal carrier was developed, and the resulted enzyme-NPG biocomposites showed extraordinary catalytic performance and stability. Compared with other existing supports for enzyme immobilization, the presented method has several advantages such as simple immobilization procedure, excellent catalytic activity, considerable enhanced operational stability, and ease of employment and recovery for reuse. These characteristics suggest that this approach provides a general strategy for the encapsulation of functional macromolecules into the pores of nanostructured materials and the resulted nano-biocomposite materials hold great potential in applications such as biosensing, molecular electronics, catalysis, and controlled delivery.
Conceived and designed the experiments: XW PX YD. Performed the experiments: XW XL PZ. Analyzed the data: XW XY. Wrote the paper: XW.
- 1. Hudson S, Cooney J, Magner E (2008) Protein in mesoporous silicates. Angew Chem Int Ed 47: 8582–8594.
- 2. Kim J, Grate JW, Wang P (2006) Nanostructures for enzyme stabilization. Chem Eng Sci 61: 1017–1026.
- 3. Nednoor P, Capaccio M, Gavalas VG, Meier MS, Anthony JE, et al. (2004) Hybrid nanoparticles based on organized protein immobilization on fullerenes. Bioconjugate Chem 15: 12–15.
- 4. Sotiropoulou S, Gavalas V, Vamvakaki V, Chaniotakis NA (2003) Novel carbon materials in biosensor systems. Biosens Bioelectron 18: 211–215.
- 5. Sotiropoulou S, Vamvakaki V, Chaniotakis NA (2005) Stabilization of enzymes in nanoporous materials for biosensor applications. Biosens Bioelectron 20: 1674–1679.
- 6. Wang Y, Frank C (2005) Mesoporous silica spheres as supports for enzyme immobilization and encapsulation. Chem Mater 17: 953–961.
- 7. Zhao HY, Zhou HM, Zhang JX, Zheng W, Zheng YF (2009) Carbon nanotube–hydroxyapatite nanocomposite: A novel platform for glucose/O2 biofuel cell. Biosens Bioelectron 25: 463–468.
- 8. Ding Y, Chen MW (2009) Nanoporous metals for catalytic and optical applications. MRS Bulletin 34: 569–576.
- 9. Ding Y, Erlebacher J (2003) Nanoporous metals with controlled multimodal pore size distribution. J Am Chem Soc 125: 7772–7773.
- 10. Ding Y, Kim YJ, Erlebacher J (2004) Nanoporous gold leaf-ancient technology/advanced material. Adv Mater 16: 1897–1900.
- 11. Kumar A, Mandal S, Selvakannan PR, Pasricha R, Mandale AB, et al. (2003) Investigation into the interaction between surface-bound alkylamines and gold nanoparticles. Langmuir 19: 6277–6282.
- 12. Qiu H, Xu C, Huang X, Ding Y, Qu Y, et al. (2008) Adsorption of laccase on the surface of nanoporous gold and the direct electron transfer between them. J Phys Chem C 112: 14781–14785.
- 13. Bradford MM (1976) A rapid and sensitive method for the quantization of microgram quantities of protein utilizing the principle of protein-dye binding. Anal Biochem 72: 248–254.
- 14. Wang X, Dou P, Zhao P, Zhao C, Ding Y, et al. (2009) Lipase immobilization on magnetic Fe3O4 nanoparticles for application in biodiesel production. ChemSusChem 2: 947–950.
- 15. Kanner J, Kinsella JE (1983) Lipid Deterioration Initiated by Phagocytic Cells in Muscle Foods: β-Carotene Destruction by a Myeloperoxidase-Hydrogen Peroxide-Halide System. J Agric Food Chem 31: 370–376.
- 16. Góth L (1991) A simple method for determination of serum catalase activity and revision of reference range. Clinica Chimica Asta 196: 143–152.
- 17. Kim KK, Song HK, Shin DH, Hwang KY, Suh SW (1997) The crystal structure of a triacylglycerol lipase from Pseudomonas cepacia reveals a highly open conformation in the absence of a bound inhibitor. Structure 5: 173–85.
- 18. Fita I, Rossmann MG (1985) The NADPH binding site on beef liver catalase. Proc Natl Acad Sci 82: 1604–1608.
- 19. Hersleth HP, Hsiao YW, Ryde U, Gorbitz CH, Andersson KK (2008) The crystal structure of peroxymyoglobin generated through cryoradiolytic reduction of myoglobin compound III during data collection. Biochem J 412: 257–264.
- 20. Ge XB, Wang RY, Liu PP, Ding Y (2007) Platinum-decorated nanoporous gold Leaf for methanol electrooxidation. Chem Mater 19: 5827–5829.
- 21. Dyal A, Loos K, Noto M, Chang SW, Spagnoli C (2003) Activity of Candida rugosa lipase immobilized on γ-Fe2O3 magnetic nanoparticles. J Am Chem Soc 125: 1684–1685.
- 22. Schlossbauer A, Schaffert D, Kecht J, Wagner E, Bein T (2008) Click chemistry for high-density biofunctionalization of mesoporous silica. J Am Chem Soc 130: 12558–12559.
- 23. Thâmara MS, Patrícia OS, Purcena LLA, Fernandes KF (2010) Study of the cashew gum polysaccharide for the horseradish peroxidase immobilization-Structural characteristics, stability and recovery. Mat Sci Eng C 30: 526–530.
- 24. Buchwald P, Bodor N (1998) Octanol-water partition of nonzwitterionic peptides: predictive power of a molecular size-based model. Proteins 30: 86–99.
- 25. Alptekin Ö, Tükel SS, Yıldırım D, Alagöz D (2010) Immobilization of catalase onto eupergit C and its characterization. J Mol Catal B: Enzym 64: 177–183.
- 26. Zhang F, Zheng B, Zhang J, Huang X, Liu H, et al. (2010) Horseradish peroxidase immobilized on grapheme oxide: physical properties and applications in phenolic compound removal. J Phys Chem C 114: 8469–8473.
- 27. Drechsler BU, Fischer NO, Frankamp BL, Rotello VM (2004) Highly efficient biocatalysts via covalent immobilization of Candida rugosa lipase on ethylene glycol-modified gold-silica nanocomposites. Adv Mater 16: 271–274.
- 28. Schmid RD, Verger R (1998) Lipases: Interfacial enzymes with attractive applications. Angew Chem Int Ed 37: 1608–1633.
- 29. Châabouni MK, Bouaziz I, Boufi S, Do Rego AMB, Gargouri Y (2009) Physical immobilization of Rhizopus oryzae lipase onto cellulose substrate: activity and stability studies. Colloids Surf B 66: 168–177.
- 30. Lu J, Nie K, Xie F, Wang F, Tan T (2007) Enzymatic sythesis of fatty acid methyl esters from lard with immobilized Candida sp. 99–125. Process Biochem 42: 1367–1370.
- 31. Noureddini H, Gao X, Philkana RS (2005) Immobilized Pseudomonas cepacia lipase for biodiesel fuel production from soybean oil. Bioresour Technol 96: 769–777.
- 32. Ravindra R, Zhao S, Gies H, Winter R (2004) Protein encapsulation in mesoporous silicate: the effects of confinement on protein stability, hydration, and volumeric properties. J Am Chem Soc 126: 12224–12225.
- 33. Zhou HX, Dill KA (2001) Stabilization of protein in confined spaces. Biochem 40: 11289–11293.
- 34. Kumar A, Mandal S, Selvakannan PR, Pasricha R, Mandale AB, et al. (2003) Investigation into the interaction between surface-bound alkylamines and gold nanoparticles. Langmuir 19: 6277–6282.
- 35. Qiu H, Xu C, Huang X, Ding Y, Qu Y, et al. (2009) Immobilization of Laccase on nanoporous gold: comparative studies on the immobilization strategies and the particles size effects. J Phys Chem 113: 2521–2525.
- 36. Kim J, Jia H, Lee C, Chung S, Kwak JH, et al. (2006) Single enzyme nanoparticles in nanoporous silica: A hierarchical approach to enzyme stabilization and immobilization. Enzym Microb Tech 39: 474–480.
- 37. Bensebaa F, Zhou Y, Deslands Y, Kruus E, Eills TH (1998) XPS study of metal-sulfur bonds in metal-alkanethiolate materials. Surf Sci 405: 472–476.
- 38. Zhang YZ, Wang X, Feng Y, Li J, Lim CT, et al. (2006) Coaxial Electrospinning of (Fluorescein Isothiocyanate-Conjugated Bovine Serum Albumin)-Encapsulated Poly(E-caprolactone) Nanofibers for Sustained Release. Biomacromolecules 7: 1049–1057.
- 39. Moreno I, González-González V, Romero-García J (2011) Control release of lactate dehydrogenase encapsulated in poly (vinyl alcohol) nanofibers via electrospinning. Eur Polym J 47: 1264–1272.