Filter quality of electret masks in filtering 14.6–594 nm aerosol particles: Effects of five decontamination methods

  • Tzu-Hsien Lin,

    Roles Formal analysis, Validation, Writing – original draft

    Affiliation Department of Dental Hygiene, China Medical University, Taichung, Taiwan

  • Chih-Chieh Chen,

    Roles Conceptualization, Funding acquisition, Resources

    Affiliation Institute of Occupational Medicine and Industrial Hygiene, National Taiwan University, Taipei, Taiwan

  • Sheng-Hsiu Huang,

    Roles Methodology, Project administration, Supervision

    Affiliation Institute of Occupational Medicine and Industrial Hygiene, National Taiwan University, Taipei, Taiwan

  • Chung-Wen Kuo,

    Roles Data curation, Formal analysis, Visualization

    Affiliation Institute of Environmental Engineering and Management, National Taipei University of Technology, Taipei, Taiwan

  • Chane-Yu Lai ,

    Contributed equally to this work with: Chane-Yu Lai, Wen-Yinn Lin

    Roles Conceptualization, Data curation, Formal analysis, Funding acquisition, Investigation, Methodology, Writing – review & editing

    cylai511@gmail.com (CYL); wylin@ntut.edu.tw (WYL)

    Affiliations Department of Occupational Safety and Health, Chung Shan Medical University, Taichung, Taiwan, Department of Occupational Medicine, Chung Shan Medical University Hospital, Taichung, Taiwan

  • Wen-Yinn Lin

    Contributed equally to this work with: Chane-Yu Lai, Wen-Yinn Lin

    Roles Conceptualization, Funding acquisition, Resources, Supervision

    cylai511@gmail.com (CYL); wylin@ntut.edu.tw (WYL)

    Affiliation Institute of Environmental Engineering and Management, National Taipei University of Technology, Taipei, Taiwan

Filter quality of electret masks in filtering 14.6–594 nm aerosol particles: Effects of five decontamination methods

  • Tzu-Hsien Lin, 
  • Chih-Chieh Chen, 
  • Sheng-Hsiu Huang, 
  • Chung-Wen Kuo, 
  • Chane-Yu Lai, 
  • Wen-Yinn Lin
PLOS
x

Abstract

This study investigates the effects of five decontamination methods on the filter quality (qf) of three commercially available electret masks—N95, Gauze and Spunlace nonwoven masks. Newly developed evaluation methods, the overall filter quality (qf,o) and the qf ratio were applied to evaluate the effectiveness of decontamination methods for respirators. A scanning mobility particle sizer is utilized to measure the concentration of polydispersed particles with diameter 14.6–594 nm. The penetration of particles and pressure drop (Δp) through the mask are used to determine qf and qf,o. Experimental results reveal that the most penetrating particle size (MPS) for the pre-decontaminated N95, Gauze and Spunlace masks were 118 nm, 461 nm and 279 nm, respectively, and the respective penetration rates were 2.6%, 23.2% and 70.0%. The Δp through the pretreated N95 masks was 9.2 mm H2O at the breathing flow rate of heavy-duty workers, exceeding the Δp values obtained through Gauze and Spunlace masks. Decontamination increased the sizes of the most penetrating particles, changing the qf values of all of the masks: qf fell as particle size increased because the penetration increased. Bleach increased the Δp of N95, but destroyed the Gauze mask. However, the use of an autoclave reduces the Δp values of both the N95 and the Gauze mask. Neither the rice cooker nor ethanol altered the Δp of the Gauze mask. Chemical decontamination methods reduced the qf,o values for the three electret masks. The value of qf,o for PM0.1 exceeded that for PM0.1–0.6, because particles smaller than 100 nm had lower penetration, resulting in a better qf for a given pressure drop. The values of qf,o, particularly for PM0.1, reveal that for the tested treatments and masks, physical decontamination methods are less destructive to the filter than chemical methods. Nevertheless, when purchasing new or reusing FFRs, penetration should be regarded as the priority.

Introduction

Standard patient care requires sterilizing or disinfecting surgical equipment and reclaimed medical devices that are contaminated by infectious agents [1]. Those items do not include masks, which should not be reused under normal circumstances. Healthcare workers (HCWs) often use disposable masks following outbreaks of SARS [24], H1N1 [5,6] MERS and influenza. In hospitals, HCWs use these masks as the front-line defense against airborne droplets and bioaerosols; however, in public, most people use the masks as a precaution or from a sense of panic.

The supply of masks may not meet demand during outbreaks or pandemics of diseases that are spread by human-to-human transmission through infectious bioaerosols. Therefore, some health authorities have considered reusing masks after decontamination to remove any infectious material. Most health authorities do not recommend the reuse of masks, but several users have attempted to use various simple methods to reclaim them to protect against noninfectious ambient particulate matter (PM)—particularly PM2.5, PM1 or PM0.1. NIOSH published a series of research articles on mask decontamination [79]. The filtering effectiveness of reclaimed filtering facepiece respirators (FFRs) and masks varies among brands and decontamination methods, so relevant results are applicable only to FFRs treated under the same conditions. Therefore, further tests must be performed to evaluate the filtration performance of filters before and after reclamation. This investigation applied three types of disposable mask, N95 FFRs (Dust Respirator 8210; 3M, St. Paul, MN, N95), gauze double-layer electret masks (Gauze, commercialized type, China) and spunlace nonwoven masks (Spunlace, Oimo, Taiwan), all of which are frequently used, and which can be reused when hospitals in Taiwan have insufficient masks for frontline healthcare workers [4].

Effective reclamation of FFRs requires low penetration of sodium chloride (NaCl) particles, and low resistance to the flow of air through the filter [7,9]. The most frequently performed tests on filtration performance involve a polydispersed aerosol and evaluation of the most penetrating particle size (MPS) [10]. NaCl and dioctyl phthalate (DOP) are adopted as challenge aerosols with count median diameters (CMD) of 75 nm±20 nm and 185 nm±20 nm, and geometric standard deviations (GSD) of 1.86 and 1.6, respectively. ISO published test conditions include a numerical median particle size distribution (PSD) of between 60 nm and 100 nm, and electromobility diameters of 160nm and 210 nm for NaCl and liquid paraffin oil, respectively [11]. Both ISO conditions involve a polydispersed aerosol with a GSD of between 1.4 and 1.8. Calculations of penetration based on the published NIOSH and ISO criteria involve the penetration of particles of all sizes, instead of the penetration of particles of any specific size. The MPSs of various FFRs are not always within the standard range of CMD. Huang et al. observed that the MPS in electret filter media varies with face velocity, fiber diameter, packing density, filter thickness and charge density [12]. Current measurement methods can provide an accurate range of penetrating PSDs [13], and elucidate the penetration and filter quality for particles covering a wide range of particle sizes.

The filter quality qf [12,1416] is a possible criterion for comparing performance of filters before and after decontamination, and is the ratio of penetration indicator to the pressure drop. The qf is also called the figure of merit (FOM) [1720]. The best filter should give the highest collection efficiency with the lowest pressure drop, where a higher qf indicates a better filter [15].

This work compares the filter qualities of three electret masks before and after the implementation of five decontamination methods that are frequently employed in Taiwan. The comparison is based on particle penetration measurements and the pressure drop through the mask. The filter quality and overall filter quality (integrated for PM0.1, PM0.1–0.6) were then calculated to measure the filtration performance.

Materials and method

Experimental procedure

Fig 1 illustrates the experimental procedure by which three types of electret mask (N95, Gauze, and Spunlace) were tested. Table 1 lists the five selected decontamination methods: (1) physical decontamination using a traditional electric rice cooker that was made in Taiwan to provide dry heat; (2) physical decontamination using an autoclave to provide moist heat, and low-temperature chemical decontamination using (3) ethanol, (4) isopropanol and (5) bleach. All of these methods are frequently adopted in hospitals in Taiwan.

Experimental system

Fig 2 shows the measured penetration of particles and the pressure drop through the test mask. In the particulate penetration test, particles were formed using a constant-output atomizer (Model 3075, TSI Inc., St. Paul, MN) to atomize potassium sodium tartrate tetrahydrate (PST) solutions into polydispersed droplets [16]. The droplets were passed through a neutralizer that contained the radiation source Kr-85 (Model 3077, TSI Inc., St. Paul, MN), which neutralized them to the Boltzmann equilibrium state. Finally, the neutralized aerosols were passed into a test chamber, and diluted in filtered air. The overall quality factor was calculated over a wide range of sizes from 14.6nm to 594 nm which include viral particle size range. To obtain this size range, a challenge aerosol size distribution was utilized with a CMD of 101 nm±10 nm, and a GSD of 2.01±0.08.

The breathing flow rate of heavy-duty workers (85 L min−1) [21] was simulated by a calculated surface velocity of 8.3 cm s−1 over the whole mask, which value is close to that used elsewhere [16]. Six pieces with a pieces with diameter 41 mm were cut from a full mask in each batch test. Each piece included the original layers to fit the filter holder, providing an effective diameter of 39 mm and a calculated effective filtration area of 11.94 cm2. To yield the specified surface velocity, the flow rate of the vacuum pump connected to each filter holder was set to 5.95 L min−1, which was maintained using a mass flow controller. A scanning mobility particle sizer (SMPS, Model 3934, TSI Inc., St. Paul, MN) was used to measure the PSDs (14.6–594 nm) upstream and downstream of the test mask. The SMPS sampling period in each test was set to 300s upscan and 30s downscan. Each decontamination type test was performed six times.

To ensure the stability of the experimental system, all flow rates in the system were controlled and monitored with mass flow controllers (Hastings Instrument, Hampton, VA), and the flow rates were adjusted using an infrared bubble meter (Gillian Instrument Co. West Caldwell, NJ).

A manometer was used to measure the pressure drop (Δp) through the test mask, and flow rates were set from 1.5 to 10 L min−1 using a mass flow controller.

Data processing

The penetration (P, %) was derived using the equation, (1) where Cd and Cu denote the concentrations of particles of the same size downstream and upstream, respectively. The filter quality factor (qf, mm H2O-1) combines P and Δp as follows [12,16].

(2)

The newly developed evaluation method—overall filter quality (qf,o, mm H2O−1) is obtained using the equation, (3)

Statistical analysis

Experimental data were analyzed using SPSS software, version 17.0 (SPSS Inc., Chicago, IL). After linear regression between the Δp and flow rate was performed, the assumption of homogeneity of the regression slopes was carried out to confirm the effects of decontamination using analysis of covariance (ANACOVA) [16]. The statistics were considered significant at p<0.05.

Results and discussion

Penetration of particles through mask before and after decontamination

Figs 37 depict the penetration of particles through the electret masks before and after decontamination using the five selected methods. Before decontamination, the particle penetration through the N95 mask did not exceed 5%. However, the penetration of particles larger than 27.9 nm through the Gauze mask exceeded 5%, and that of particles from 14.1 nm to 594 nm through the Spunlace mask exceeded 8.6% (Fig 3). According to Fig 3, the penetration of particles through the test masks following heating in the rice cooker was similar to that before heating. Treating the masks in an autoclave increased the penetration of particles through the Spunlace and Gauze masks (Fig 4). Figs 57 reveal that treating the test masks with ethanol, bleach or isopropanol raised the penetration of particles, (especially larger ones. Submersion in bleach significantly changed the penetration through the N95 masks (Fig 6).

thumbnail
Fig 3. Penetration of particles through mask after decontamination using rice cooker.

https://doi.org/10.1371/journal.pone.0186217.g003

thumbnail
Fig 4. Penetration of particles through mask after decontamination using autoclave.

https://doi.org/10.1371/journal.pone.0186217.g004

thumbnail
Fig 5. Penetration of particles through mask after decontamination using ethanol.

https://doi.org/10.1371/journal.pone.0186217.g005

thumbnail
Fig 6. Penetration of particles through mask after decontamination using bleach.

https://doi.org/10.1371/journal.pone.0186217.g006

thumbnail
Fig 7. Penetration of particles through mask after decontamination using IPA.

https://doi.org/10.1371/journal.pone.0186217.g007

Electret fibrous filters, which were used in the masks were tested in this investigation, are highly representative of such respirators. For a given fiber diameter, packing density, and thickness, electret filters have much higher filtration efficiency than non-electret filters, particularly for submicron aerosols [12]. To assess the effect of charge density on filtration efficiency, filters were dipped in isopropanol to remove charges before measuring the filter quality [2]. The charge density of filters strongly affected the filtration efficiency. Reducing the charge density increased aerosol penetration. Treatment of N95 masks with isopropanol increased the penetration of particles larger than 50 nm, owing to a reduction in the charge density of the filter.

The experimental results indicate that decontamination by dry heat in a rice cooker had little effect on the penetration of particles through any of the tested masks (Fig 3), while wet heat in the autoclave had little effect on that of the N95 mask (Fig 4). From a previous study [8], the penetration of N95 masks that were sealed in a standard poly/paper autoclave bag and then treated in an autoclave, as measured using a TSI Model 8130 automated filter tester, increased from 0.7% to 18.7% (p = 0.003). However, in the same study, the penetration of particles had little effect on the N95 masks that were treated with tap water (p = 0.417) or dry heat at a temperature of 80°C (p = 0.192). The major discrepancies of penetration of particles between pretreated and treated masks were discussed in the later section of MPS.

Chemical methods that involved submersion in liquid ethanol, isopropanol or bleach influenced the penetration of particles through the electret masks, probably because alcohols and bleach eliminated the electrostatic charges on the filters [22], and characteristics such as fiber diameter, packing density and charge density determined the ultimate effect [12]. Bleach destroys the structure of Gauze filters. Treatment with bleach seriously damaged the structure of the filter in the double-layer static Gauze mask used in this study, preventing it from being tested further (Fig 6). Similarly, FFR melted under microwave irradiation or dry heat starting at 100°C. [9].

The penetrations of particles before and after decontamination were experimentally compared using particles of traditional standard sizes for penetration tests. The standard sizes were 75 nm [10] and 300 nm for electret masks and mechanical filter filtration [12], respectively. The results thus indicate that decontamination increased the penetration of both 75 nm and 300 nm particles through the masks (p<0.05), except in the cases of decontamination of N95 masks in a rice cooker or an autoclave, and Gauze and Spunlace masks in a rice cooker (Fig 8). Moreover, Spunlace masks treated by ethanol did not statistically significant increase the penetration of 300 nm particles (p = 0.093).

thumbnail
Fig 8. Penetration of 75nm and 300nm particles through mask.

* indicates p<0.05.

https://doi.org/10.1371/journal.pone.0186217.g008

Most penetrating particle size (MPS)

The experimental MPS values of the pretreated N95, Gauze, and Spunlace masks were 118 nm, 461 nm and 279 nm, respectively (Table 2). All of the MPS values of the pretreated masks exceeded 75 nm, and that of the Gauze masks exceeded 300nm. The MPS value of the N95 masks increased upon decontamination, except when using the rice cooker (Table 2). Most of the MPS values following decontamination exceeded 300 nm, except for N95 treated with dry heat using the rice cooker, for which the MPS remained at 118 nm, and the penetration at 118 nm remained approximately 2.6%. The MPS value was 346 nm for autoclave-treated N95 masks and larger than pretreated ones (118 nm). These results are comparable and only matches to an earlier finding condition that aerosol penetration decrease and MPS increase with decreasing face velocity (mechanical filter) [22]. However, autoclave is a common sterilization method and further study on FFRs is necessary.

thumbnail
Table 2. Most penetrating particle sizes (MPS, nm), associated penetration (P, %) and direction of change in pressure drop (Δp).

https://doi.org/10.1371/journal.pone.0186217.t002

The MPS value following immersion in bleach was 300 nm, satisfying the requirements for a mechanical filter [12]. The MPS of the decontaminated Gauze was between 414 nm and 496 nm. Decontamination increased the MPS of Spunlace to more than 400 nm. These results are consistent with an earlier finding that both aerosol penetration and MPS increase with decreasing charge density [22].

Effect of decontamination on pressure drop through masks

For the N95 masks before decontamination, Δp increased from 1.7 mm H2O to 16.8 mm H2O as the flow rate increased from 1.5 L min−1 to 10.2 L min−1; decontamination using ethanol produced similar results (p = 0.869) (Fig 9(A)). For the N95 masks submerged in bleach for 10 min, Δp linearly increased from 4.9 mm H2O at 1.5 L min−1 to 39.2 mm H2O at 10.2 L min−1 (p<0.001). Comparable results were found when using rice cooker (p = 0.019). However, the Δp of the autoclaved N95 masks fell (p<0.001). The measured values of Δp (9.2 mm H2O) at a flow rate of 5.95 L min−1 were less than 35 mm H2O, which is the upper limit for inhalation as specified in 42 CFR 84 subpart K [10].

thumbnail
Fig 9. Pressure drop through mask before and after decontamination.

* indicates p<0.05; # indicates the Gauze masks were destroyed and therefore their Δp could not be obtained.

https://doi.org/10.1371/journal.pone.0186217.g009

For the Gauze masks before decontamination, Δp increased from 0.5 mm H2O to 7.1 mm H2O as the flow rate increased from 1.5 L min−1 to 10.2 L min−1. Similar results were obtained following decontamination using the rice cooker (p = 0.893) or ethanol (p = 0.201) (Fig 9(B)). When the Gauze masks were decontaminated using the autoclave, Δp linearly fell from 0.6 mm H2O at 1.5 L min−1 to 5.9 mm H2O at 10.2 L min−1 (p<0.001). However, the Gauze masks were destroyed when they were submerged in bleach, and therefore their Δp could not be obtained.

For the Spunlace masks before decontamination, Δp increased from 0.2 mm H2O to 2.5 mm H2O as the flow rate rose from 1.5 L min−1 to 10.2 L min−1, and sharper slopes were obtained following treatment by a rice cooker, ethanol, bleach, and an autoclave (p≤0.01) (Fig 9(C)).

The flowrate through the filter influences pressure drop. Thus, masks of all three types exhibited a linear relationship between pressure drop and flowrate following the application of each of the decontamination methods. Immersion in bleach increased the pressure drop through the N95 mask (to 40 mm H2O at a flowrate of 10 L min−1), whereas use of the autoclave reduced it. Similar results were obtained in the tests on the Gauze masks except when bleach was used, because bleach destroyed all of the masks.

Decontamination typically increased Δp, but treatment in the autoclave did not do so for the N95 or Gauze masks. The low pressure drop results for these two types of masks were observed to be associated with folds of the inner and outer filter supports. These folds may reduce the uniformity of filter density, causing the air to flow through loose filter material in the mask, and reducing the resistance of the filter. From the observation, as show in Fig 10, the outer layer of the masks were deformed, shrunken and stiff and these phenomena were similar to a previous study [8]. But no remarkable mottle was observed. However, the characteristics of various filters are not easily obtained as this information is commercially sensitive, and this fact imposed a limitation on this study.

Moreover, in the study, the calculated inspiratory breathing resistance (IBR) at 85 L min-1 [23] was 6.5, 2.6 and 0.9 mm H2O/L/sec for the pretreated N95, Gauze and Spunlace masks, respectively. Previously reported maximum value for the normal threshold for detection of IBR was 7.6 mm H2O/L/sec [23]. In the study, the highest IBR value was 15.3 mm H2O/L/s for the N95 masks submerged in bleach which was the only one exceeded 7.6 mm H2O/L/sec. All the other IBR values of treated masks ranged from 1.0–7.4 mm H2O/L/s. The pressure drop probably playing a role if inhalation resistance exceeded 35 mm H2O (equal to 24.7 mm H2O/L/s), but since few of the masks came close to that, the primary concerning factor of qf should focus on filter penetration.

Filter quality before and after decontamination

The qf values in this work were computed from the penetration of particles and the pressure drop through the filter. Most calculated qf values were between 0.1 and 1, and this parameter was found to be a function of particle diameter (Fig 11(A)–11(C)). The highest values of qf were obtained for smaller particle diameters, and the lowest values were obtained for particle diameters of around 400–500 nm, which was the range of experimental MPS in this investigation (Table 2).

Regulation US 42 CFR part 84 requires that the resistances of particulate respirators upon initial exhalation and inhalation do not exceed 25 mm H2O and 35 mm H2O, respectively [10], and the calculated qf values are 0.117 mm H2O−1 and 0.084 mm H2O−1, respectively (Fig 11(A)–11(C)). All of the values of qf that were obtained in the test exceeded the calculated values, indicating that all of the masks satisfied the calculated qf values (0.117 mm H2O−1 and 0.084 mm H2O−1) after decontamination. However, qf incorporates two variables, namely aerosol penetration and pressure drop. The minimum filtering efficiency (≥95% for N95, for example) should be considered before obtaining qf.

Figs 11(D)–11(F) present the calculated ratios of qf values before and after decontamination. Most of the qf ratios of the N95 masks were less than 1.0, except when treatment involved the autoclave or ethanol (Fig 11(D)). The pressure drop (Fig 9(A)), which is the denominator in qf, decreased when decontaminating N95 masks using the autoclave. Decontaminating N95 masks using ethanol did not affect the penetration of particles with diameters of less than 33.4 nm (Fig 6), and yielded a qf ratio of close to unity. Under the Boltzmann charge equilibrium, approximately 60% of particles with diameters of less than 50 nm were uncharged [15].

Similar results were observed in the test involving the Gauze mask (Fig 11(E)). Most of the qf ratios for Spunlace masks were less than 1.0 (Fig 11(F)). In most of the tests, the ratio of qf values decreased as the particle size increased.

Overall filter quality, qf,o

Since qf is a function of particle size, qf,o was calculated using Eq (3), in which the value of qf is weighted by particle size ranging from 14.6 nm to 594 nm. Table 3 presents the relevant results, including the full range of sizes and qf,o values for particles that are smaller and larger than 100 nm (PM0.1, PM0.1–0.6), and the ratio of qf,o values before and after decontamination. The values of qf, o for pretreated N95, Gauze and Spunlace masks over the full range of particle sizes were 0.69 mm H2O−1, 0.92 mm H2O−1, and 1.07 mm H2O−1, respectively. The pretreated Spunlace masks had the highest qf,o because they had the lowest pressure drop (Fig 9). Before decontamination, the N95 mask had the lowest qf,o over the full range of particle sizes and for PM0.1–0.6. The factor that most strongly influenced these results was the pressure drop, which was highest for the N95 mask (Fig 9). The Spunlace mask had the lowest value of qf,o for PM0.1–0.6, because it had the highest penetration (Figs 36).

thumbnail
Table 3. Overall filter quality and ratio of values before and after decontamination.

https://doi.org/10.1371/journal.pone.0186217.t003

Decontamination decreased all values of qf,o over the full range of particle sizes (Table 3). The ratios of qf,o values ranged from 0.33 (for N95 immersed in bleach) to 0.98 (for autoclaved N95 and Gauze masks). Similar results were obtained for PM0.1–0.6, for which the ratios ranged from 0.2 (N95 immersed in bleach) to 0.91 (Gauze mask in the rice cooker). However, for PM0.1, qf,o increased upon treatment in three cases, which were the autoclaved N95, the autoclaved Gauze masks and the ethanol-immersed Gauze masks. The N95 immersed in bleach had the lowest qf,o value. In all tests, qf,o for PM0.1 exceeded that for PM0.1–0.6 because particles smaller than 100 nm penetrate less, reflecting higher filtration quality for a given pressure drop. The qf,o values indicate that physical decontamination methods are better than chemical methods, especially for PM0.1.

A good respirator should have a high overall value of qf, including low aerosol penetration and a low pressure drop. Basically, Table 3 would suggest that Gauze and Spunlace masks are the best because they have a higher qf than N95 masks due to their low pressure drop. However, respirator selection should prioritize penetration and fit factor and not qf. Neither mask in the study meets criteria for penetration despite their high qf. In current study, only the tested N95 masks matched the minimum 42 CFR Part 84 criteria [10] because they had both an acceptable pressure drop and penetration. In 2011, Viscusi et al. [24] demonstrated that incubation in moist heat significantly reduced the fit factor of two of the six FFRs (p < 0.05). For these two FFRs, fit factors after decontamination remained ≥100. In our study, neither qf nor qf,o consider fit factor when considering mask performance. Since the fit factor importantly affects the effectiveness of a worn mask, the end users should also consider the effect of decontamination on fit. This investigation did not evaluate the bioefficacy of each FFR following treatments. Our research group will publish results on these topics elsewhere.

Conclusion

Decontamination increases the MPS, and changes the qf,o of N95, Spunlace and Gauze masks. Filter quality decreased as the particle size increased due to an increase in penetration. Decontamination increased the pressure drop, except for N95 and Gauze masks that were decontaminated using an autoclave. Decontamination reduced the value of qf,o, unless performed by using an autoclave or rice cooker, which created observable folds of the masks.

Instruments currently used for measuring particle size distributions can be used to measure the qf,o over the full range of particle sizes in this study, in order to select decontaminated masks. However, different particle sizers can be used with different size ranges, so calculated values of qf,o ought to be associated with corresponding PSDs. Moreover, a particle sizer with a size range that better covers the MPS of the test masks should be used to study the effect of particle size on qf,o.

The Spunlace mask had a higher qf,o value than the N95 FFR, and seemed to perform better, but it provided minimal protection because of the high penetration. Consequently, buyers of FFRs or masks must consider both the penetration and the pressure drop. A good respirator should have a low aerosol penetration as the most important characteristic. Since the breathing resistance of N95 is 9.2 mm H2O at 5.95 L min−1, the wearer may not notice a difference in pressure drop after decontamination. Therefore, for N95 respirators with a pressure drop below a 35 mm H2O threshold, the aerosol penetration must be kept below 5% consistent with 42 CFR 84 subpart K [10]. Moreover, it should be noted that the calculation of qf and qf,o provides more weight on pressure drop for comparing respirator after decontamination, therefore, qf and qf,o should be used carefully.

Supporting information

S1 File. Penetration & pressure drop.

This is the data of Fig 3 to Fig 7.

https://doi.org/10.1371/journal.pone.0186217.s001

(XLSX)

References

  1. 1. Taiwan CDC. Infection Control Manual for Medical Care Facilities. 2014.
  2. 2. Chen YC, Chen PJ, Chang SC, Kao CL, Wang SH, Wang LH, et al. Infection control and SARS transmission among healthcare workers, Taiwan. Emerg Infect Dis. 2004; 10: 895–898. pmid:15200825
  3. 3. Twu SJ, Chen TJ, Chen CJ, Olsen SJ, Lee LT, Fisk T, et al. Control measures for severe acute respiratory syndrome (SARS) in Taiwan. Emerg Infect Dis. 2003; 9: 718–720. pmid:12781013
  4. 4. Tzeng HM. SARS infection control in Taiwan: investigation of nurses’ professional obligation. Outcomes Manag Nurs Pract. 2003; 7: 186–193.
  5. 5. CDC. Interim Guidance on Infection Control Measures for 2009 H1N1 Influenza in Healthcare Settings, Including Protection of Healthcare Personnel, 14 October, 2009. http://www.cdc.gov/swineflu/guidelines_infection_control.htm.
  6. 6. WHO. Infection prevention and control in health care for confirmed or suspected cases of pandemic (H1N1) 2009 and influenza-like illnesses, 25 June 2009, http://www.who.int/csr/resources/publications/20090429_infection_control_en.pdf.
  7. 7. Bergman MS, Viscusi DJ, Heimbuch BK, Wander JD, Sambol AR, Shaffer RE. Evaluation of multiple (3-Cycle) decontamination processing for filtering facepiece respirators. JEFF. 2010; 4: 33–41.
  8. 8. Viscusi DJ, King WP, Shaffer RE. Effect of decontamination on the filtration efficiency of two filtering facepiece respirator models. J Int Soc Respir Prot. 2007; 24: 93–107.
  9. 9. Viscusi DJ, Bergman MS, Eimer BC, Shaffer RE. Evaluation of five decontamination methods for filtering facepiece respirators. Ann Occup Hyg. 2009; 53: 815–826. pmid:19805391
  10. 10. NIOSH. Respiratory protection devices. Title 42, Code of Federal regulation, Part 84. Washington, DC: U.S. Government Printing Office, Office of the Federal Register; 2011. pp. 548–612.
  11. 11. ISO. ISO 16900–3: Respiratory protective devices—Methods of test and test equipment—Part 3: Determination of particle filter penetration. International Standards Organisation General Secretariat, Switzerland, 2012.
  12. 12. Huang SH, Chen CW, Kuo YM, Lai CY, McKay R, Chen CC. Factors affecting filter penetration and quality factor of particulate respirators. Aerosol Air Qual Res. 2013; 13: 162–171.
  13. 13. Fonseca AS, Viana M, Pérez N, Alastuey A, Querol X, Kaminski H, et al. Intercomparison of a portable and two stationary mobility particle sizers for nanoscale aerosol measurements. Aerosol Sci Technol. 2016; 50: 653–668.
  14. 14. Brown RC. Air Filtration. Pergamon Press, London. 1993.
  15. 15. Hinds WC. Aerosol Technology: Properties, Behavior, and Measurement of Airborne Particles, Wiley-Interscience, New York, 1999, pp. 183–205.
  16. 16. Lin TH, Tang FC, Chiang CH, Chang CP, Lai CY. Recovery of bacteria in filtering facepiece respirators and effects of artificial saliva/perspiration on bacterial survival and performance of respirators. Aerosol Air Qual Res. 2017; 17: 187–197.
  17. 17. Dhaniyala S, Liu BYH. Investigations of particle penetration in fibrous filters: Part II. Theoretical. JIEST. 1999; 42: 40–46.
  18. 18. Kalayci V, Ouyang M, Graham K. Polymeric nanofibres in high efficiency filtration applications. Filtration. 2006; 6: 286–293.
  19. 19. Wang J, Kim SC, Pui DYH. Figure of merit of composite filters with micrometer and nanometer fibers. Aerosol Sci Technol. 2008; 42: 722–728.
  20. 20. Wang J, Kim SC, Pui DYH. Investigation of the figure of merit for filters with a single nanofiber layer on a substrate. J Aerosol Sci. 2008; 39: 323–334.
  21. 21. Brosseau LM, McCullough NV, Vesley D. Mycobacterial aerosol collection efficiency by respirator and surgical mask filters under varying conditions of flow and humidity. Appl Occup Environ Hyg. 1997; 12: 435–445.
  22. 22. Chen CC, Huang SH. The effects of particle charge on the performance of a filtering facepiece. Am Ind Hyg Assoc J. 1998; 59: 227–233. pmid:9586197
  23. 23. Roberge RJ, Kim J-H, Powell JB, Shaffer RE, Ylitalo CM, Sebastian JM. Impact of low filter resistances on subjective and physiological responses to filtering facepiece respirators. PLoS ONE. 2013; 8(12): e84901. pmid:24386434
  24. 24. Viscusi DJ, Bergman MS, Novak DA, Faulkner KA, Palmiero A, Powell J, et al. Impact of three biological decontamination methods on filtering facepiece respirator fit, odor, comfort, and donning ease. J Occup Environment Hyg. 2011; 8: 426–436.