Reducing Strength Prevailing at Root Surface of Plants Promotes Reduction of Ag+ and Generation of Ag0/Ag2O Nanoparticles Exogenously in Aqueous Phase

Abstract

Potential of root system of plants from wide range of families to effectively reduce membrane impermeable ferricyanide to ferrocyanide and blue coloured 2,6-dichlorophenol indophenol (DCPIP) to colourless DCPIPH2 both under non-sterile and sterile conditions, revealed prevalence of immense reducing strength at root surface. As generation of silver nanoparticles (NPs) from Ag+ involves reduction, present investigations were carried to evaluate if reducing strength prevailing at surface of root system can be exploited for reduction of Ag+ and exogenous generation of silver-NPs. Root system of intact plants of 16 species from 11 diverse families of angiosperms turned clear colorless AgNO3 solutions, turbid brown. Absorption spectra of these turbid brown solutions showed silver-NPs specific surface plasmon resonance peak. Transmission electron microscope coupled with energy dispersive X-ray confirmed the presence of distinct NPs in the range of 5–50 nm containing Ag. Selected area electron diffraction and powder X-ray diffraction patterns of the silver NPs showed Bragg reflections, characteristic of crystalline face-centered cubic structure of Ag0 and cubic structure of Ag2O. Root system of intact plants raised under sterile conditions also generated Ag0/Ag2O-NPs under strict sterile conditions in a manner similar to that recorded under non-sterile conditions. This revealed the inbuilt potential of root system to generate Ag0/Ag2O-NPs independent of any microorganism. Roots of intact plants reduced triphenyltetrazolium to triphenylformazon and impermeable ferricyanide to ferrocyanide, suggesting involvement of plasma membrane bound dehydrogenases in reduction of Ag+ and formation of Ag0/Ag2O-NPs. Root enzyme extract reduced triphenyltetrazolium to triphenylformazon and Ag+ to Ag0 in presence of NADH, clearly establishing potential of dehydrogenases to reduce Ag+ to Ag0, which generate Ag0/Ag2O-NPs. Findings presented in this manuscript put forth a novel, simple, economically viable and green protocol for synthesis of silver-NPs under ambient conditions in aqueous phase, using root system of intact plants.

Citation: Pardha-Saradhi P, Yamal G, Peddisetty T, Sharmila P, Nagar S, Singh J, et al. (2014) Reducing Strength Prevailing at Root Surface of Plants Promotes Reduction of Ag+ and Generation of Ag0/Ag2O Nanoparticles Exogenously in Aqueous Phase. PLoS ONE 9(9): e106715. https://doi.org/10.1371/journal.pone.0106715

Editor: Vipul Bansal, RMIT University, Australia

Received: December 31, 2013; Accepted: August 9, 2014; Published: September 3, 2014

Copyright: © 2014 Pardha-Saradhi et al. This is an open-access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.

Funding: Yamal and Shilpi thank Council for Scientific and Industrial Research (Govt. of India) for providing research fellowship. Sharmila thanks the Department of Biotechnology (Govt. of India) for financial support under Bio-CARe Women Scientist Scheme. The funders had no role in study design, data collection and analysis, decision to publish, or preparation of the manuscript.

Competing interests: The authors have declared that no competing interests exist.

Introduction

Nanotechnology has witnessed spectacular advancement in fabrication and utilization of nanomaterials. Owing to small size and large surface to volume ratio, nanoparticles possess unique physicochemical and biological properties which differ entirely from the bulk material. Amongst different metal nanoparticles, the synthesis and application of silver NPs received wide attention, as silver nanoparticles find application in almost every sphere of life. Due to immense antimicrobial properties, silver NPs find wide application in medicine especially artificial teeth, bone coating, medical catheters, wound dressings besides surgical instruments. Silver nanoparticles are also extensively used in daily commodities such as cosmetics (viz. lotions, creams etc.), toothpastes, detergents, soaps, surface cleaners, room sprays, shoe insoles and textiles. Utility of silver nanoparticles in home appliances (such as washing machines, air and water filters), automotive upholstery, paints and food storage containers is also known [1]–[4]. Silver NPs find usefulness in sensing applications such as biolabeling, optical imaging of cancer and detection of DNA sequences [5], [6]. Electronic application of silver nanoparticles includes its usage for the preparation of optical devices, inks for circuit boards, high density recording devices, battery-based intercalation materials [6]–[9]. Large surface area of silver NPs provides high surface energy for catalysis [10]. Silver NPs of different sizes and shapes are routinely synthesized by various chemical and physical methods [11]–[13]. Various physical, chemical and physico-chemical approaches such as ion sputtering, laser ablation, inert gas condensation, mechanical milling, thermal or laser irradiation, chemical reduction, sol-gel technique, photochemical reduction and electrochemical techniques have so far been employed to generate metal NPs [12]–[14]. The Lee-Meisel method using sodium citrate along with heating for 1 h for generation of silver nanoparticles continues to be the standard by which other synthetic methods are compared. Although, the method is simple, however, it produces broad distribution of particle size in range of 20–600 nm [15], [16]. Recently, we demonstrated potential of biomolecules/components viz. yeast extract and mannitol to generate silver nanoparticles in size range of 10–50 and 10–20 nm, respectively, upon autoclaving with AgNO3 for 30 min at 121°C under a pressure of 1.06 kg/cm2. We had categorically reported that mannitol being a compatible solute (i.e. does not have any reported negative impact on living systems) can be exploited for large scale production of silver nanoparticles within a narrow range [11]. Although, this method reported by us is rapid, it required high temperature and pressure.

Owing to negative aspects of physical and chemical methods researchers across the globe have felt the need to develop alternate green/biological methods for generating NPs [17]–[19]. With an urge to develop environmentally benign green methods researchers looked at possible use of living systems, their components or dead biomass for synthesis of silver and other noble metal nanoparticles. Till date, researchers used (i) a variety of microorganisms, their cell free extracts and dead biomass (bacteria, actinomycetes and fungi) [11], [20]–[24]; (ii) cell organelles like chloroplasts [25]; (iii) extract from various components (viz. leaves, seeds, flowers, fruit or fruit peel, latex, tuber, bark etc.) of numerous plant species [17], [24]–[28] and (iii) live plants (which generate nanoparticles within their cells) to generate metal nanoparticles [26]–[32]. However, these biological methods also have certain limitations, such as (i) use of microorganism requires special facilities for their maintenance and safety measures [32]; (ii) it is difficult to precisely identify the biomolecule(s) amongst the cocktail of molecules in extracts of various biological materials/components, that are responsible for generation of silver NPs; (iii) it would be difficult to extract NPs synthesized intracellular in cells of plants or microorganisms and moreover, due to the presence of wide variety of biomolecules (having reducing strength) within the cells, NPs formed intracellular would be of broad size/shape range (31–32). In search for an alternate andideal green method, we felt it wise to exploit root system of intact plants for generating silver nanoparticles, as plant biologists clearly established that root system of plants possess immense reducing strength [32]–[36] and generation of metal nanoparticles from ions primarily involves reduction [10], [11], [31], [32], [36]. Therefore, the present investigations were carried with the aim to evaluate the potential of plants to generate silver nanoparticles exogenously at the root surface. To the best of our knowledge, no research team so far has made any efforts to evaluate if plant species possess potential to exogenously generate Ag NPs at the root surface. In this communication, using 16 plant species from 11 diverse taxonomic groups of angiosperms we are reporting for the first time that the roots system of intact plants can be exploited for exogenous generation of silver nanoparticles. We have also elaborated on the advantages of using root system of intact plants for rapid bulk synthesis of silver nanoparticles.

Materials and Methods

Plant material

Sixteen plant species from 11 distinct families of diverse taxonomic groups of Angiosperms were collected from wild and maintained garden beds of North/Main campus of University of Delhi, details of which are given in Table 1. In all the cases utmost care was taken to cause least damage to the plants as well as to the root system at the time of collection.

thumbnail
Download:
Table 1. Details of plant species used for exogenous generation of silver NPs by root system of intact plants.

https://doi.org/10.1371/journal.pone.0106715.t001

Raising plants under sterile conditions

Seeds of Brassica juncea cv. Varuna, Vigna mungo cv. PS-1, and Lycopersicon esculentum cv. Pusa Ruby were purchased from Seed Sales Counter, Indian Agricultural Research Institute (IARI), New Delhi, and that of Triticum aestivum cv. H1-1544 and Cicer arietinum cv. PG-114, were gifted by Dr. A.N. Mishra (Head, IARI Regional Station, Indore, India) and Dr. Jitendra Kumar (Principal Scientist, Pulse Division, IARI, New Delhi, India), respectively. Seeds were treated with 0.5% cetrimide for 5 min, washed with distilled water; surface sterilized with 0.1% (w/v) mercuric chloride for 3 min and washed thoroughly with sterile distilled water. Capped glass bottles of (2.5×5″) dimensions containing glass beads (∼75 g) with 25 ml of mineral growth medium [consisting of 2500 mg L−1 KNO3, 250 mg L−1 MgSO4, 150 mg L−1 CaCl2, 150 mg L−1 NaH2PO4, 134 mg L−1 (NH4)2SO4, 10 mg L−1 MnSO4, 3 mg L−1 H3BO3, 2 mg L−1 ZnSO4, 0.75 mg L−1 KI, 0.25 mg L−1 Na2MoO4 and iron source (27.8 mg L−1 FeSO4 and 37.3 mg L−1 EDTA)] [37] were sterilized by autoclaving at a pressure of 1.06 Kg cm−2 and at temperature of 121°C for 30 min. Surface sterilized seeds were sown in these bottles under sterile conditions, in laminar air flow. For present investigations 20 day old plants of L. esculentum, 9–10 day old plants of B. juncea, C. arietinum, and 4–5 day old plants of T. aestivum and V. mungo were carefully removed from glass beads with least damage to the root system, and incubated for 6–12 h in AgNO3 solution.

Determining root surface redox activity

In order to determine reduction potential associated with root surface, roots of intact plants were submerged in 0.1 mM DCPIP solutions. Reduction potential of roots of intact plants was determined by monitoring decrease in the optical density at 600 nm due to reduction of DCPIP to DCPIPH2. Capacity of roots of intact plants to reduce DCPIP was expressed in terms of nano moles of DCPIP reduced h−1g−1 root fresh weight. Reduction potential associated with roots of intact plants of different plant species was also determined using ferricyanide which is a membrane impermeable electron acceptor [32]–[35]. Potassium ferricyanide {K3[Fe(CN)6]} was used at 1 mM concentration for evaluating redox activity of roots. The reduction of ferricyanide was recorded by measuring decrease in the optical density at 420 nm. Capacity of roots of intact plants to reduce ferricyanide was expressed in terms of nmoles of ferricyanide reduced h−1g−1 root fresh weight.

All experiments were conducted atleast five independent times. The data expressed as mean ±SE have been statistically analyzed using ANOVA (Analysis of Variance) through SPSS (Statistical Package for Social Sciences) version 16.0. The differences between means were tested for significance by Duncan's multiple range test (DMRT) at p≤0.05.

Incubation of plants with salt solutions

For evaluating the impact of Ag+, and potential of plants to generate silver NPs, plants were exposed to different concentrations (viz. 0.5, 1 and 2 mM) of silver nitrate (AgNO3) solutions, prepared in double distilled water. All the plants placed in various salt solutions were incubated at room temperature (25±2°C) with a 16/8 h light/dark cycle. White fluorescent light (Phillips, India) with a light intensity of 120 µmol m−2 s−1 photon flux density was used for illuminating the plants.

Incubation of plants under strict sterile conditions with salt solutions

For evaluating potential of plants to generate Ag-NPs they were exposed to different concentrations (viz. 0.01, 0.05, 0.1, 0.25, 0.5, and 1 mM) of AgNO3 prepared in sterile double distilled water. Plants were incubated at room temperature (25±2°C) with a 16/8 h light/dark cycle with a light intensity of 120 µmol m−2 s−1 photon flux density. For experiments carried under strict sterile conditions the stock solutions of filter sterilized Ag was used. Different concentrations were prepared from this stock using sterile double distilled water in laminar air flow. The glassware(s) used in these experiments were sterilized by autoclaving at a pressure of 1.06 Kg cm−2 and at temperature of 121°C for 30 min. After washing roots 2–3 times with sterile double distilled water, the plants raised under sterile conditions were transferred to 25×200 mm sterile Borosil tubes with their roots immersed in sterile salt solutions, in laminar air flow. The exogenously generated silver nanoparticles were characterized through UV-Vis spectral studies, TEM investigations coupled with EDX and PXRD studies.

UV-Vis spectral studies

UV-Vis absorption spectra of various test solutions in which roots of intact plants were submerged for different time intervals were recorded between 190–1100 nm using Specord 200 Analytikjena UV-Vis spectrophotometer. The formation of Ag nanoparticles was indicated by the appearance of characteristic absorption peak generally at 410–480 nm.

Transmission electron microscopic (TEM) investigations

AgNO3 solutions incubated with roots of intact plants for duration of ∼24 h were collected and subjected to sonication for 30 min to minimize primary particle agglomeration. 10 µl of the resulting colloidal solution was drop coated onto a 200-mesh copper grid covered with an ultrathin continuous C film in a desiccator. The grids were viewed in transmission electron microscope of Technai G2 T30 U-TWIN at a voltage of 300 kV. Hardware associated with the machine also allowed (i) energy dispersive X-ray (EDX spectra), and (ii) Selected area electron diffraction (SAED) pattern measurements. EDX spectra indicated the composition of isolated nanoparticles and SAED patterns indicated the crystalline/amorphous nature of the nanoparticles that were fabricated and released by the plants into the solutions.

Powder X-ray diffraction (PXRD) Studies

AgNO3 solutions incubated with roots of intact plants was drop coated on Silica surface and dried. The PXRD pattern was collected using Rigaku Rotaflex RAD-B or Bruker or Pan Analytika instruments using Cu target CuK(α) at the rate of 0.020 step in 1.2 s in the 2 theta range 30–80°.

Detection of proteins, amino acids or phenolics in incubation medium

Roots of intact plants were incubated in sterile double distil water for a duration of 24 h. This incubation medium was then tested for the presence of proteins, phenolics and amino acids using standard protocols [38]–[40].

Comparative study of roots of plants with sodium citrate

The efficiency of roots of plants was compared to one of the most widely used reductant viz. sodium citrate. The stock solution of AgNO3 was filter sterilized and various concentrations viz. 0.01, 0.05, 0.1, 0.25, 0.5 and 1 mM were prepared using sterile double distilled water.

Determination of dehydrogenase activity

In vitro.

Roots of (i) Triticum aestivum seedlings (4–5 d old) raised under sterile conditions; and (ii) Portulaca grandiflora plants raised in earthen pots were homogenized independently in 50 mM phosphate buffer (pH-7.2) containing 5 mM EDTA and 5% of polyvinylpyrrolidone and centrifuged at 16000 xg at 4°C. Supernatant was used as the crude enzyme extract for determining dehydrogenase activity following modified protocol of Yamauchi and co-workers [41]. The reaction mixture for determining the dehydrogenase activity consisting of 500 µl crude enzyme extract, 10 µmoles of 2,3,5-triphenyltetrazolium chloride and 2 µmoles of NADH in a final volume of 4 ml of 100 mM phosphate buffer (pH 7.6), was incubated at 37°C for 6 h. Subsequently, the reaction mixtures were centrifuged at 10000 xg for 20 min and the pellet was dissolved in 4 ml ethanol. The quantity of 1,3,5-triphenylformazan formed due to dehydrogenase activity was determined by taking absorbance at 484 nm. The dehydrogenase activity was finally expressed as nmoles of formazan formed g−1 fresh weight of root h−1.

Simultaneously, the potential of dehydrogenases present in crude enzyme extract to reduce Ag+ and form silver-NPs determined by incubating 500 µl of crude enzyme extract with 100 mM phosphate buffer (pH-7.6) containing 1 µmole AgNO3 and 2 µmoles NADH in a final volume of 4 ml at 37°C for 6 h. The presence of silver-NPs in resultant reaction mixture was confirmed by (i) absorption spectra which showed Ag-NPs specific peak; (ii) transmission electron microscope.

In vivo.

Roots of intact plants, of (i) Triticum aestivum (4–5 d old) raised under sterile conditions; and (ii) Portulaca grandiflora raised in earthen pots, were incubated in phosphate buffer (pH- 7.6) containing either 2,3,5-triphenyltetrazolium chloride or 0.25 mM AgNO3. After incubating for different time intervals (6 to 24 h), (i) resultant incubation medium was centrifuged at 10000 xg for 20 min and the pellet consisting of 1,3,5-triphenylformazan was dissolved in 95% ethanol; and (ii) root system of plants were excised, cut in to segments and dipped in 95% ethanol for 12 h to extract out 1,3,5-triphenylformazan. The formazan formed due to dehydrogenase activity was determined by measuring absorbance at 484 nm. The dehydrogenase activity was finally expressed as nmoles of formazan formed g−1 fresh weight of root h−1.

Results and Discussion

It is well established that generation of silver nanoparticles similar to other metal nanoparticles primarily involves reduction of their ions [10], [11]. Earlier, it had been unequivocally proven that root system of plant species possess strong reducing capacity [32]–[36].

During present investigations root system of intact plants of all 16 plant species, from 11 diverse families of angiosperms effectively reduced artificial electron acceptors (DCPIP) and ferricyanide within duration of 6-12 h. As is evident from Fig. 1 root system of plants reduced (i) blue colored DCPIP to colorless DCPIPH2 and (ii) ferricyanide to ferrocyanide. Earlier, Rubinstein and co-workers recorded reduction of membrane impermeable ferricyanide to ferrocyanide in the solutions in which roots of intact plants were incubated [34]–[35]. Our findings similar to the findings of Rubinstein et al. [34] clearly established that root surface could exogenously reduce ferricyanide to ferrocyanide. This prompted us to test if root system of intact plants can exogenously reduce Ag+ to Ag0 at the root surface and generate silver nanoparticles in aqueous phase under ambient conditions.

thumbnail
Download:
Figure 1. Potential of root system of plants to reduce DCPIP (0.1 mM) and ferricyanide (1 mM).

Reduction of DCPIP (a–d) and ferricyanide (c–d) by root system of intact plants of Lycopersicon esculentum (Le), Brassica juncea (Bj), Vigna mungo (Vm), Cicer arietinum (Ca), Ocimum sanctum (Os), Catharanthus roseous (Cr), Cynodon dactylon (Cd), Cannabis sativa (Cs), Phyllanthus fraternus (Pf), Portulaca grandiflora (Pg), Triticum aestivum (Ta) and Vernonia cinerea (Vc) under non-sterile (a–c) and sterile (d) conditions. Ctrl represents 0.1 mM DCPIP. Vertical lines on bars represent mean ± standard error, n = 5. Values designated by different letters above bars are significantly different between plant species at p ≤ 0.05 level (Duncan's multiple range test).

https://doi.org/10.1371/journal.pone.0106715.g001

As anticipated, root system of intact plants of all plant species tested, altered color of clear AgNO3 solution, turbid brown, within a duration of 6–12 h (Fig. 2a–e), probably due to reduction of Ag+ and formation of silver nanoparticles. It is known that clear AgNO3 solutions turn brown upon generation of silver nanoparticles [11], [42]. In general, the UV-Vis absorption spectra of these brown colored colloidal solutions showed absorption maxima between 380 to 450 nm (Fig. 3). Absorption peak in this range has been reported to arise due to surface plasmon resonance in silver NPs [11]. The intensity and position of absorption peak varied depending on the concentration of Ag+ and plant species used (Fig. 3).

thumbnail
Download:
Figure 2. Potential of root system of intact plants to generate silver NPs.

Root system of intact plants of (a) Phyllanthus fraternus, (b) Portulaca grandiflora, (c) Triticum aestivum, (d) Amaranthus gracilis and (e) Vernonia cinerea exhibitingpotential to alter clear colorless AgNO3 of different concentrations (mM) turbid brown. No color change noted in the tubes containing different concentrations of AgNO3 incubated under similar conditions without plants (a–d).

https://doi.org/10.1371/journal.pone.0106715.g002

thumbnail
Download:
Figure 3. UV-Vis absorption spectra of 0.5, 1.0 and 2 mM AgNO3 exposed to root system of intact plants of different plant species for 12 h.

https://doi.org/10.1371/journal.pone.0106715.g003

Transmission electron microscopic (TEM) investigations confirmed the presence of distinct NPs in brown colloidal solutions that resulted due to incubation of root system of intact plants in AgNO3 solutions (Figs. 4–6, Table 1). In general, the NPs were in the range of 5–50 nm and spherical (Figs. 4–6). These results are in accordance with the UV-Vis absorption spectra of the colored colloidal solutions that showed surface plasmon resonance (SPR) peak centered around 430 nm, implying the presence of spherical NPs [43]. Energy dispersive X-ray (EDX) studies confirmed the presence of Ag in these NPs (Figs. 4–6). The EDX pattern (Figs. 4–6) collected from these nanoparticles showed distinct peaks at 3.40 keV and 22 keV corresponding to Ag, while the peaks situated at binding energies of 8.06 and 1 keV correspond to Cu and C, respectively. The peaks of C and Cu arose due to their presence as an integral component of carbon coated copper grids. The presence of distinct rings corresponding to Bragg reflections in selected area electron diffraction (SAED) pattern established that these silver NPs were crystalline (Figs. 4–6).

thumbnail
Download:
Figure 4. TEM images (a–c), SAED (d–f) and EDX (g–i) of silver NPs synthesized exogenously by root system of intact plants of Tagetes erecta (a, d, g), Catharanthus roseous (b, e, h), Euphorbia hirta (c, f, i).

SAED show Bragg reflections characteristic of crystalline Ag0 () and Ag2O (*).

https://doi.org/10.1371/journal.pone.0106715.g004

thumbnail
Download:
Figure 5. TEM (a–c), SAED (d–f) and EDX (g–i) of silver NPs synthesized exogenously by roots system of intact plants of Brassica juncea (a, d, g), Cicer arietinum (b, e, h), and Phyllanthus fraternus (c, f, i).

SAED show Bragg reflections characteristic of crystalline Ag0 () and Ag2O (*).

https://doi.org/10.1371/journal.pone.0106715.g005

thumbnail
Download:
Figure 6. TEM (a–d), SAED (e–h) and EDX (i–l) of silver NPs synthesized exogenously by root system of intact plants of Cynodon dactylon (a, e, i), Portulaca grandiflora (b, f, j), Lycopersicon esculentum (c, g, k) and Vernonia cinerea (d, h, l).

SAED show Bragg reflections characteristic of crystalline Ag0 () and Ag2O (*).

https://doi.org/10.1371/journal.pone.0106715.g006

Powder X-ray diffraction (PXRD) patterns of silver nanoparticles generated exogenously by root surface of intact plants showed presence of distinct peaks, corroborating their crystalline nature. Irrespective of the plant species used, the PXRD patterns of silver nanoparticles formed exogenously by root of intact plants matched with the standard diffraction pattern of Joint Committee on Powder Diffraction Standards (JCPDS) No. 89–3722, confirming the face-centered cubic (fcc) structure of Ag0, and 76–1393 characteristic of Ag2O with cubic geometry (Fig. 7). These PXRD results revealed that the silver nanoparticles formed by the root surface of plant species are constituted of Ag0 and Ag2O. During earlier investigations also we recorded susceptibility of Ag0 NPs to oxidation and accordingly, recorded formation of a mixture of Ag0/Ag2O NPs by yeast extract, mannitol as well as yeast extract-mannitol medium [11]. Levard and co-workers [44] also reported the susceptibility of Ag0 NPs to oxidation under ambient conditions [44]. Therefore, we believe that some of the Ag0 NPs formed by reduction of Ag+ at the root surface were oxidized to Ag2O NPs in aqueous phase under ambient conditions. Recently, we also reported that the root surface of plants possesses potential to form iron oxy-hydroxide NPs [36].

thumbnail
Download:
Figure 7. PXRD pattern of silver NPs.

The PXRD pattern of silver NPs synthesized exogenously by roots system of intact plants of various plant species showing Bragg reflections characteristic of crystalline face-centred cubic structure of Ag0 () and cubic structure of Ag2O (*).

https://doi.org/10.1371/journal.pone.0106715.g007

Possible mechanism of generation of silver nanoparticles at the root surface

Earlier, two plant species namely, Medicago sativa (alfalfa) and Brassica juncea (mustard) which are considered to be metallophytes have been reported to synthesize silver nanoparticles within their cells [29]–[31]. Gardea-Torresdey et al. [29] reported that alfalfa roots absorb Ag0 from agar medium and transfer it to shoot in the same oxidation state, where these silver atoms (Ag0) arrange themselves to form nanoparticles. However, these researchers neither addressed the mode of reduction of Ag+ to Ag0 in agar medium nor discussed about any factor (if any) responsible for arrangement of Ag0 to form nanoparticles in the shoots. Harris and Bali [30] noted formation of silver nanoparticles within the cells of plants of M. sativa and B. juncea exposed to AgNO3 solution, but these researchers also remained silent on mode of reduction of Ag+ and generation of Ag nanoparticles. Subsequently, Beattie & Haverkamp [31] reported synthesis of silver nanoparticles in cells of B. juncea, predominantly in chloroplast. The later researchers believed that the reducing sugars could play a role in reduction of Ag+ and generation of silver NPs. However, plant cells besides having reducing sugars also possess number of other biomolecules such as phenolics, organic acids, amino acids etc. which have been shown to be potent reductants for reduction of Ag+ to generate silver nanoparticles [22], [27], [45].

During present investigations, root system of all plant species tested possessed potential to exogenously reduce Ag+ and form silver nanoparticles when incubated with AgNO3 solution. Roots of plants are known to exude a variety of biomolecules viz. organic acids, amino acids, phenolics etc. [46] which have been shown to possess capacity to reduce Ag+ and generate silver nanoparticles [11], [47], [48]. To evaluate if capacity of root system of plants to reduce Ag+ and generate Ag nanoparticles exogenously, recorded during present investigations is due to biomolecules that are exuded by the roots, 2 sets of investigations were carried. In the first set of investigations, we tested for presence of phenolics, amino acids and proteins in the medium in which roots of intact plants were incubated for 24 h, but, did not find any detectable levels of these biomolecules. Subsequently, the incubation medium in which roots of intact plants were incubated for 24 h, was tested directly for its potential to generate silver nanoparticles. Neither color change nor presence of any silver nanoparticles was recorded. However, as stated above roots of intact plants incubated in AgNO3 solution could reduce Ag+ and generate silver nanoparticles within a duration of 6–12 h. Infact, earlier researchers also categorically demonstrated that the reduction of membrane impermeable ferricyanide to ferrocyanide is not due to any of the lechates from the roots [34], [35]. Therefore, our findings clearly indicated that the exogenous reduction of Ag+ and generation of silver nanoparticles by root surface of intact plants within a duration of 6–12 h is not due to biomolecules (if any) released by the root system of intact plants.

Another likely possibility for the exogenous generation of silver nanoparticles could be due root associated microorganisms, as microorganisms can generate silver nanoparticles [21], [22]. Infact, it has been reported that the root associated microorganisms are involved in the reduction of metal ions [49], [50]. In order to validate if microorganisms (if any) harbored by the root system in any way are essential for reduction of Ag+ and generation of silver nanoparticles exogenously, investigations were carried with Brassica juncea, Triticum aestivum, Vigna mungo, Cicer arietinum and Lycopersicon esculentum plants under strict sterile conditions.

Root system of all the plant species raised and assessed under strict sterile conditions turned clear colorless AgNO3 solutions turbid brown (Fig. 8). These turbid brown solutions like those formed by the plants from non-sterile conditions showed (i) silver NPs specific SPR peak in their absorption spectra (Fig. 8); and (ii) distinct crystalline NPs constituted of Ag (Fig. 9). Also, the PXRD patterns of NPs formed under sterile conditions (Fig. 9), similar to those formed under non-sterile conditions matched with JCPDS No. 89–3722, and 76–1393, indicating presence of Ag0 and Ag2O. These investigations ruled out the necessity of root associated microorganisms in reduction of Ag+ and formation of silver NPs exogenously by root surface of plants.

thumbnail
Download:
Figure 8. Potential of sodium citrate and root system of intact plants of 4 day old Vigna mungo and Triticum aestivum to generate silver NPs.

1% sodium citrate (a) and root system of intact plants of V. mungo (b) and T. aestivum (c) incubated in AgNO3 of different concentrations (mM) for 6 h, showing alteration in color and turning clear solution colloidal under sterile conditions at room temperature. UV-Vis spectra of resultant colloidal solutions formed by 1% sodium citrate (d), V. mungo (e) and T. aestivum (f).

https://doi.org/10.1371/journal.pone.0106715.g008

thumbnail
Download:
Figure 9. TEM images (a–b), SAED (c–d), EDX (e–f) and PXRD (g–h) of silver NPs synthesized exogenously by root system of intact plants of Vigna mungo (a, c, e, g) and Triticum aestivum (b, d, f, h).

Bragg reflections characteristic of crystalline face-centred.

https://doi.org/10.1371/journal.pone.0106715.g009

The root system of plants could effectively reduce ferricyanide to ferrocyanide and DCPIP to colorless DCPIPH2 even under strict sterile conditions. Ferricyanide being membrane impermeable, its reduction to ferrocyanide must be occurring exogenously at the root surface, which is also evident from investigations of Rubinstein and co-workers [34]. It is known that ferri to ferro reduction potential (0.430 V) which is significantly higher compared to Ag+ to Ag0 (0.7991 V) in SHE series [31], [51]. Therefore, root system of plants which have potential to reduce ferricyanide to ferrocynaide can be a powerful system for reduction of Ag+ to Ag0, at the root surface and form silver NPs.

It is established that plasma membrane of root surface cells possess transmembrane dehydrogenases/reductases, which play a critical role in root surface mediated reduction processes by drawing electrons from NAD(P)H [33], [34], [52]. This well established fact, makes us believe that the plasma membrane bound dehydrogenase(s)/reductase(s) of root surface cells must have effectively reduced Ag+ to Ag0 through oxidation of NAD(P)H to NAD(P)+. A hypothetical model summarizing the mechanism of reduction of Ag+ to Ag0 and formation of silver NPs catalyzed by plasma membrane bound dehydrogenase/ reductase is shown in Fig. 10.

thumbnail
Download:
Figure 10. Schematic representation of the mechanism involved in the reduction of Ag+ and formation of silver NPs at the root surface of live plants.

https://doi.org/10.1371/journal.pone.0106715.g010

Establishing potential of dehydrogenases to generate silver-NPs

Roots of intact plants of intact plants of (i) Triticum aestivum (raised under sterile conditions); and (ii) Portulaca grandiflora reduced clear 2,3,5-triphenyltetrazolium chloride to colloidal pink-purple 1,3,5-triphenylformazan at their surface (Fig. 11) confirming the presence of dehydrogenases in association with root surface cells. Reduction of clear 2,3,5-triphenyltetrazolium chloride to colloidal pink-purple 1,3,5-triphenylformazan is comparable to the conversion of clear AgNO3 solution colloidal brown by the root system of intact plants (Fig. 11).

thumbnail
Download:
Figure 11. Evidences demonstrating - the presence of dehydrogenases in association with root surface cells (a, b); and the potential of dehydrogenases to reduce triphenyltetrazolium to triphenylformazan and Ag+ to Ag0 (which in turn generate Ag0/Ag2O-nanoparticles) (c).

(a) and (b) displays root system of intact plants of Portulaca grandiflora incubated in phosphate buffer (pH 7.6) in absence (A) and presence of triphenyltetrazolium chloride (B) or AgNO3 (C). Note colour change due to formation of triphenylformazan (B) and silver-nanoparticles (C). (c) depicts tubes with reaction mixture (100 mM phosphate buffer pH 7.6) containing - root enzyme extract with NADH (D); root enzyme extract with triphenyltetrazolium chloride (E); root enzyme extract with triphenyltetrazolium chloride and NADH (F); AgNO3 with NADH (G); AgNO3 with root enzyme extract (H); and AgNO3 with root enzyme extract and NADH (I), 6 h after incubation at 37°C. Please note colour change due to formation of triphenylformazan (F) and silver nanoparticles (I). (d) shows silver nanoparticles from tube (I) formed due to dehydrogenase activity in presence of NADH. (e) depicts absorption spectra of the reaction mixtures from tubes (G), (H) and (I). Note silver nanoparticle specific absorption peak that intensified due to dehydrogenase activity in presence of NADH.

https://doi.org/10.1371/journal.pone.0106715.g011

Root enzyme extracts of both Triticum aestivum and Portulaca grandiflora reduced triphenyltetrazolium to triphenylformazan in presence of NADH, confirming the presence of dehydrogenase activity (Table 2; Fig. 11). Root enzyme extracts of these plant species turned reaction mixture (phosphate buffer, pH 7.6) containing AgNO3, colloidal brown within a duration of 3 to 6 h at 37°C, in presence of NADH (Fig. 11). Absorption spectra of these colloidal brown solutions showed presence of silver-NPs specific plasmon resonance peak. Transmission electron microscopic investigations revealed presence of silver-NPs in these solutions. These findings unequivocally demonstrated that dehydrogenases present in the enzyme extract possess potential to reduce Ag+ to Ag0 and promote formation of silver-NPs.

thumbnail
Download:
Table 2. Dehydrogenase activities recorded at the surface of roots of intact plants (in vivo) and in root enzyme extracts (in vitro).

https://doi.org/10.1371/journal.pone.0106715.t002

Advantages of employing root system of intact plants for generation of silver NPs

Biological methods for synthesis of nanoparticles are considered to be superior over various physical and chemical methods [18]. Successful generation of silver NPs using variety of microorganisms and plant extracts has been most widely reported. However, due to limitations none of these methods could be used for commercial production of silver NPs. Use of microorganism requires special facilities for their maintenance and safety measures [26]. Amongst microorganisms, even pathogenic microorganisms such as Klebsiella pneumonia, Bacillus subtilis, Micrococcus luteus, Serratia marcescens, Aspergillus etc. have been employed for generation of silver NPs [21]. However, the serious concern for the use of such pathogenic microorganisms would be likely emergence of new pathogenic strains resistant to silver NPs that are otherwise widely used as antimicrobial agents. Although, synthesis of silver NPs using extracts of various plant materials was reported to be superior, it is difficult to precisely identify the biomolecule(s) amongst the cocktail of molecules in these extracts that are responsible for generation of silver NPs.

Similarly, the potential of live plants to synthesize silver NPs intracellularly cannot be exploited for commercial production due to practical difficulties in their extraction. Moreover, due to the presence of wide variety of biomolecules (having reducing strength) in the cells, intracellularly formed NPs would be of broad size range. Accordingly, Beattie and Haverkamp [31] observed nanoparticles in the range of 2–100 nm in cells of B. juncea plants exposed to silver salt solutions. In contrast, during present investigations potential of root system of intact plants to exogenously generate silver NPs was realized. Moreover, the silver NPs formed exogenously by root system were in narrow size range. Most importantly, these exogenously generated silver NPs can be harvested with ease.

Amongst chemical methods Lee Miesel protocol for synthesis of silver nanoparticles using sodium citrate continues to remain a standard method, with which newly invented methods are compared [16]. In this popular Lee Meisel method 10 ml of 1% sodium citrate is added to 500 ml of boiling AgNO3 solution, and the resultant mixture is boiled for 1 h for synthesis of silver NPs. The major limitation of this method is the production of silver NPs in broad size range i.e. 20–600 nm [15], [16]. In contrast, during present investigations, roots of intact plants of all 16 plant species tested synthesized silver NPs at room temperature within the size range of 5–50 nm.

The potential of root system of intact plants of V. mungo and T. aestivum to generate silver NPs was compared with that of sodium citrate at room temperature and under strict sterile conditions. 0.02% sodium citrate (i.e. used for generation of silver NPs in the Lee Meisel method) failed to show any alteration in color of the AgNO3 solution or silver NPs specific SPR peak in the absorption spectra even after incubating for duration of 12 h at room temperature. As is evident from Fig. 8 root system of intact plants of V. mungo and T. aestivum incubated under ambient and sterile conditions altered the color of clear AgNO3 solution colloidal brown within 6 h and the absorption spectra of these colloidal solutions showed silver NPs specific SPR peak. Although, sodium citrate when used at a concentration 50 times higher than that used in Lee Meisel method, turned clear colorless AgNO3 solutions grayish colloidal, the intensity of color and silver NPs specific SPR peak in the absorption spectra of these colloidal solutions was significantly less than that recorded when root system of intact plants were used, under ambient conditions (Fig. 8). The dynamic light scattering (DLS) studies showed that the mean particle size of silver NPs synthesized using 1 mM AgNO3, by the root system of intact plants of V. mungo and T. aestivum was ∼20 nm, while those synthesized in presence of 1% sodium citrate was ∼33 nm under ambient conditions. These findings, clearly demonstrate that root system of intact plants can be employed for rapid synthesis of silver NPs under ambient conditions. To the best of our knowledge, the novel method of using root system of intact plants for bulk synthesis of silver NPs under ambient conditions would be most green, simple and economically viable.

Conclusions

The findings presented in this manuscript demonstrated for the first time that root system of intact plants possess immense potential to reduce Ag+ and form Ag0/Ag2O NPs. Using 16 plant species from 11 diverse families, it has been demonstrated that the root system of all angiosperms possess reducing strength that can be aptly used for reduction of metal ions like Ag+. Root system of plants could reduce Ag+ and generate Ag0/Ag2O NPs even under strict sterile conditions, establishing that root system alone possess immense reducing strength. Efficacy of root system of these plant species to reduce membrane impermeable ferricyanide to ferrocyanide and triphenyltetrazolium to triphenylformazan established that plasma membrane bound dehydrogenases/reductases are responsible for reduction of Ag+ at surface, and exogenous generation of Ag0/Ag2O NPs. Dehydrogenases in root enzyme extract possessed potential to reduce Ag+ to Ag0 and generate Ag0/Ag2O NPs in the presence of NADH. As the plasma membrane bound dehydrogenases seems to be a single major component for reduction of Ag+ the NPs generated were relatively more or less spherical and in narrow size range. The findings presented in this communication also established that synthesis of Ag0/Ag2O NPs by root system of intact plants is superior over all the biological methods reported so far. To the best of our knowledge, this novel method for generation of silver NPs is most green, simple, and economically viable.

Acknowledgments

We are thankful to Dr. A.N. Mishra (Head, IARI Regional Station, Indore, India) and Dr. Jitendra Kumar (Principal Scientist, Pulse Division, IARI, Pusa Institute, New Delhi, India) for providing seeds of Triticum aestivum and Cicer arietinum, respectively. We acknowledge the support rendered by the Director and staff of University Science Instrumentation Facility (USIC), University of Delhi. We are thankful to Mr. Harsh and Mr. Rahul Bhardwaj for assistance during PXRD and TEM analysis.

Author Contributions

Conceived and designed the experiments: PPS. Performed the experiments: PPS GY PS TP SN JS. Analyzed the data: PPS GY PS SN JS RN. Contributed reagents/materials/analysis tools: PPS KSR. Wrote the paper: PPS GY PS TP SN JS RN KSR.

References

  1. 1. Song JY, Kwon EY, Kim BS (2010) Biological synthesis of platinum nanoparticles using Diopyros kaki leaf extract. Bioproc Biosyst Eng 33: 159–164.
  2. 2. Alvarez-Puebla RA, Aroca RA (2009) Synthesis of silver nanoparticles with controllable surface charge and their application to surface-enhanced Raman scattering. Anal Chem 81: 2280–2285.
  3. 3. Singh N, Manshian B, Jenkins GJS, Griffiths SM, Williams PM, et al. (2009) NanoGenotoxicology: The DNA damaging potential of engineered nanomaterials. Biomaterials 30: 3891–3914.
  4. 4. Tolaymat TM, Badawy AME, Genaidy A, Scheckel KG, Luxton TP, et al. (2010) An evidence-based environmental perspective of manufactured silver nanoparticle in syntheses and applications: A systematic review and critical appraisal of peer-reviewed scientific papers. Sci Total Environ 408: 999–1006.
  5. 5. Jain D, Daima HK, Kachhwaha S, Kothari SL (2009) Synthesis of plant-mediated silver nanoparticles using papaya fruit extract and evaluation of their anti microbial activities. Dig J Nanomat Biostruc 4: 557–563.
  6. 6. Wiley BJ, Chen Y, McLellan JM, Xiong Y, Li Z, et al. (2007) Synthesis and optical properties of silver nanobars and nanorice. Nano Lett 7: 1032–1036.
  7. 7. Navaladian S, Viswanathan B, Varadarajan TK, Viswanath RP (2008) Microwave-assisted rapid synthesis of anisotropic Ag nanoparticles by solid state transformation. Nanotechnology 19: 1–7.
  8. 8. Kim SH, Choi BS, Kang K, Choi Y, Yang SI (2007) Low temperature synthesis and growth mechanism of Ag nanowires. J Alloy Compd 433: 261–264.
  9. 9. Deshmukh RD, Composto RJ (2007) Surface segregation and formation of silver nanoparticles created in situ in poly(methyl methacrylate) films. Chem Mater 19: 745–54.
  10. 10. Xia Y, Xiang Y, Lim B, Skrabalak SE (2008) Shape-Controlled Synthesis of Metal Nanocrystals: Simple Chemistry Meets Complex Physics? Angew Chem Int Ed 48: 60–103.
  11. 11. Yamal G, Sharmila P, Rao KS, Pardha-Saradhi P (2013b) Inbuilt potential of YEM medium and its constituents to generate Ag/Ag2O nanoparticles. PLoS ONE 8(4): e61750.
  12. 12. Masala O, Seshadri R (2004) Synthesis routes for large volumes of nanoparticles. Annu Rev Mater Res 34: 41–81.
  13. 13. Daniel MC, Astruc D (2004) Gold nanoparticles: assembly, supramolecular chemistry, quantum-size-related properties, and applications toward biology, catalysis, and nanotechnology. Chem Rev 104: 293–346.
  14. 14. Wani IA, Khatoon S, Ganguly A, Ahmed J, Ganguli AK, et al. (2010) Silver nanoparticles: Large scale solvothermal synthesis and optical properties. Mater Res Bull 45: 1033–1038.
  15. 15. Rycenga M, Cobley CM, Zeng J, Li W, Moran CH, et al. (2011) Controlling the synthesis and assembly of silver nanostructures for plasmonic applications. Chem Rev 111: 3669–3712.
  16. 16. Evanoff DD Jr, Chumanov G (2005) Synthesis and optical properties of silver nanoparticles and arrays. Chem Phys Chem 6: 1221–1231.
  17. 17. Mittal AK, Chisti Y, Banerjee UC (2013) Synthesis of metallic nanoparticles using plant extracts. Biotechnol Adv 31: 346–356.
  18. 18. Iravani S (2011) Green synthesis of metal nanoparticles using plants. Green Chem 13: 2638–2650.
  19. 19. Dahl JA, Maddux BLS, Hutchison JE (2007) Toward greener nanosynthesis. Chem Rev 107: 2228–2269.
  20. 20. Zhang X, Yan S, Tyagi RD, Surmapalli RY (2011) Synthesis of nanoparticles by microorganisms and their application in enhancing microbiological reaction rates. Chemosphere 82: 489–494.
  21. 21. Narayanan KB, Sakthivel N (2010) Biological synthesis of metal nanoparticles by microbes. Adv Colloid Interfac 156: 1–13.
  22. 22. Mohanpuria A, Rana NK, Yadav SK (2008) Biosynthesis of nanoparticles: technological concepts and future applications. J Nanopart Res 10: 507–517.
  23. 23. Klaus-Joerger T, Joerger R, Olsson E, Granqvist CG (2001) Metal-accumulating bacteria and their potential for materials science Trends Biotechnol. 19: 15–20.
  24. 24. Yamal G, Sharmila P, Rao KS, Pardha-Saradhi P (2013) Yeast Extract Mannitol medium and its constituents promote synthesis of Au nanoparticles. Process Biochem 48: 532–538.
  25. 25. Shabnam N, Pardha-Saradhi P (2013) Photosynthetic electron transport system promotes synthesis of Au-nanoparticles. PLoS ONE 8(8): e71123.
  26. 26. Gan PP, Li SFY (2012) Potential of plant as a biological factory to synthesize gold and silver nanoparticles and their applications. Rev Environ Sci Biotechnol 11: 169–206.
  27. 27. Kumar V, Yadav SK (2009) Plant-mediated synthesis of silver and gold nanoparticles and their applications. J Chem Technol Biotechnol 84: 151–157.
  28. 28. Shabnam N, Pardha-Saradhi P, Sharmila P (2014) Phenolics impart Au3+-stress tolerance to cowpea by generating nanoparticles. PLoS ONE 9(1): e85242.
  29. 29. Gardea-Torresdey JL, Gomez E, Peralta-Videa JR, Parsons JG, Troiani H, et al. (2003) Alfalfa sprouts: a natural source for the synthesis of silver nanoparticles. Langmuir 19: 1357–1361.
  30. 30. Harris AT, Bali R (2008) On the formation and extent of uptake of silver nanoparticles by live plants. J Nanopart Res 10: 691–695.
  31. 31. Beattie IR, Haverkamp RG (2011) Silver and gold nanoparticles in plants: sites for the reduction to metal. Metallomics 3: 628–632.
  32. 32. Pardha-Saradhi P, Yamal G, Peddisetty T, Sharmila P, Singh J, et al. (2014) Root system of live plants is a powerful resource for the green synthesis of Au-nanoparticles. RSC Adv. 4: 7361–7367.
  33. 33. Vuletic M, Sukalovic VHT, Vucinic Z (2005) The Co-existence of the oxidative and reductive systems in roots. The role of plasma membranes. Ann N Y Acad Sci 1048: 244–258.
  34. 34. Rubinstein B, Stern AI, Stout RG (1984) Redox activity at the surface of oat root cells. Plant Physiol 76: 386–391.
  35. 35. Qiu ZS, Rubinstein B, Stern AI (1985) Evidence for electron transport across the plasma membrane of Zea mays root cells. Planta 165 : 383 391.
    • 36. Pardha-Saradhi P, Yamal G, Peddisetty T, Sharmila P, Singh J, et al. (2013) Plants fabricate Fe-nanocomplexes at root surface to counter and phytostabilize excess ionic Fe. Biometals 27: 97–114.
    • 37. Arora S, Pardha-Saradhi P (1995) Light-induced enhancement in proline levels in Vigna radiata exposed to environmental stresses. Aust J Plant Physiol 22: 383–386.
    • 38. Bradford MM (1976) A rapid and sensitive method for the quantitation of microgram quantities of protein utilizing the principle of protein-dye binding. Analytical Biochem 72: 248–254.
    • 39. Ainsworth EA, Gillespie KM (2007) Estimation of total phenolic content and other oxidation substrates in plant tissues using Folin-Ciocalteu reagent. Nat Protoc 2: 875–877.
    • 40. Starcher B (2001) A ninhydrin-based assay to quantitate the total protein content of tissue samples. Analyt Biochem 292: 125–129.
    • 41. Yamauchi T, Watanabe K, Fukazawa A, Mori H, Abe F, et al. (2014) Ethylene and reactive oxygen species are involved in root aerenchyma formation and adaptation of wheat seedlings to oxygen-deficient conditions. J Exptl Bot 65: 261–27342.
    • 42. Njagi EC, Huang H, Stafford L, Genuino H, Galindo HM, et al. (2011) Biosynthesis of iron and silver nanoparticles at room temperature using aqueous Sorghum bran extracts. Langmuir 27: 264–271.
    • 43. Yang Y, Matsubara S, Xiong L, Hayakawa T, Nogami M (2007) Solvothermal synthesis of multiple shapes of silver nanoparticles and their SERS properties. J Phys Chem C 111: 9095–9104.
    • 44. Levard C, Hotze EM, Lowry GV, Brown GE Jr (2012) Environmental transformations of silver nanoparticles: Impact on stability and toxicity. Environ Sci Technol 46: 6900–6914.
    • 45. Leela A, Vivekanandan M (2008) Tapping the unexploited plant resources for the synthesis of silver nanoparticles. Afr J Biotechnol 7: 3162.
    • 46. Dong J, Mao WM, Zhang GP, Wu FB, Cai Y (2007) Root excretion and plant tolerance to Cadmium toxicity-a review. Plant Soil Environ 53: 193–200.
    • 47. Darroudi M, Ahmad MB, Abdullah AH, Ibrahim NA (2011) Green synthesis and characterization of gelatin-based and sugar-reduced silver nanoparticles. Int J Nanomed 6: 569–574.
    • 48. Wang W, Chen O, Jiang C, Yang D, Liu X, et al. (2007) One-step synthesis of biocompatible gold nanoparticles using gallic acid in the presence of poly-(N-vinyl-2-pyrrolidone). Colloid Surface A 301: 73–79.
    • 49. Emerson D, Weiss JV, Megonigal JP (1999) Iron oxidizing bacteria are associated with ferric hydroxide precipitates (Fe-Plaque) on the roots of wetland plants. Appl Environ Microbiol 65: 2758–2761.
    • 50. Weiss JV, Emerson D, Backer SM, Megonigal JP (2003) Enumeration of Fe(II)-oxidizing and Fe(III)-reducing bacteria in the root zone of wetland plants: Implications for a rhizosphere iron cycle. Biogeochemistry 64: 77–96.
    • 51. Huang TH, Salter G, Kahn SL, Gindt YM (2007) Redox titration of ferricyanide to ferrocyanide with ascorbic acid: illustrating the Nernst equation and Beer–Lambert law. J Chem Educ 81: 1461–1463.
    • 52. Crane FL, Sun IL, Barr R, Low H (1991) Electron and proton transport across the plasma membrane. J Bioenerg Biomembr 23: 773–803.