Hydrogels have become a promising research focus because of their potential for biomedical application. Here we explore the long-range, electrostatic interactions by following the effect of trans-acting (pH) and cis-acting factors (peptide mutation) on the formation of Au-phage hydrogels. These bioinorganic hydrogels can be generated from the bottom-up assembly of Au nanoparticles (Au NP) with either native or mutant bacteriophage (phage) through electrostatic interaction of the phage pVIII major capsid proteins (pVIII). The cis-acting factor consists of a peptide extension displayed on the pVIII that mutates the phage. Our results show that pH can dictate the direct-assembly and stability of Au-phage hydrogels in spite of the differences between the native and the mutant pVIII. The first step in characterizing the interactions of Au NP with phage was to generate a molecular model that identified the charge distribution and structure of the native and mutant pVIII. This model indicated that the mutant peptide extension carried a higher positive charge relative to the native pVIII at all pHs. Next, by monitoring the Au-phage interaction by means of optical microscopy, elastic light scattering, fractal dimension analysis as well as Uv-vis and surface plasmon resonance spectroscopy, we show that the positive charge of the mutant peptide extension favors the opposite charge affinity between the phage and Au NP as the pH is decreased. These results show the versatility of this assembly method, where the stability of these hydrogels can be achieved by either adjusting the pH or by changing the composition of the phage pVIII without the need of phage display libraries.
Citation: Souza GR, Yonel-Gumruk E, Fan D, Easley J, Rangel R, Guzman-Rojas L, et al. (2008) Bottom-Up Assembly of Hydrogels from Bacteriophage and Au Nanoparticles: The Effect of Cis- and Trans-Acting Factors. PLoS ONE 3(5): e2242. doi:10.1371/journal.pone.0002242
Editor: Jianren Lu, The University of Manchester, United Kingdom
Received: January 31, 2008; Accepted: April 2, 2008; Published: May 21, 2008
Copyright: © 2008 Souza et al. This is an open-access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.
Funding: G.S. is a Scholar from the Odyssey Program at The University of Texas M.D. Anderson Cancer Center and a recipient of the Breast Cancer Concept Award from DOD. R.R. is also a Scholar from the Odyssey Program at The University of Texas M.D. Anderson Cancer Center. This work was supported by a grant from the Department of Defense and by an award from the Gillson-Longenbaugh Foundation (to W.A. and R.P.). Besides funding the work, the sponsors did not have any role in designing or conducting these studies.
Competing interests: The authors have declared that no competing interests exist.
Bottom-up nanoparticle assembly has recently been considered as a model for the development of enabling technologies in bioengineering and biomedical research , . Tailoring nanoparticle architecture requires the challenge of reproducibly manipulating and controlling assembly at the molecular level. The integration of inorganic nanoparticles into biological systems, by means of synthetic biology fabrication, may offer solutions needed to overcome such tasks. Bioinorganic assembly, such as aggregates of nanoparticles and filamentous bacteriophage  (phage), have shown many potential applications, ranging from cancer cell targeting, bio-materials/electronics, to stem cell tissue engineering , , , , , , . For large-scale fabrication of hybrid structures, one relies on controlling the various types of non-covalent interactions, long-range (i.e. electrostatic) and short-range (i.e. van der Waals) , , , , typically between nanoparticles and proteins, in which chemical and structural complexity makes elucidation of the assembly mechanism difficult to fully characterize.
Here we explore the long-range, electrostatic interactions by following the effect of pH on the assembly of Au-phage hydrogels. Hydrogels have become a promising research focus because of their potential broad biomedical application, including tissue engineering, wound healing, drug/gene delivery and stem cell manipulation. In our work, bioinorganic assemblies are generated from the cross-linking of Au nanoparticles with either native or mutant phage through electrostatic interaction of the pVIII major capsid proteins (pVIII). An alternative approach to the controlled assembly of nanoparticles onto phage has been presented in which peptide selection for metal binding is performed through display on the pIII minor capsid protein (pIII) followed by genetic manipulation of the phage's pVIII to display the selected peptide , . Both the native pVIII and the library-selected amino acid sequences of the metal-binding peptides show a low frequency of the typical amino acids that have the highest affinity for metals , , such as histidines and cysteines , , . Electrostatic interactions play a major role in the stabilization and functionality of bioinorganic molecules , , ,  and one would expect that charge-mediated forces contribute to the building and stability of phage and Au NP assembly. The assembly and stability of the Au-phage hydrogels likely results from a complex interplay of ligand-exchange , long- and short-range interactions, which include electrostatic forces (long-range nature). Here, we focus on addressing the contribution of electrostatic interactions in the onset and stability of the hydrogel assembly as a function of phage major capsid composition. We show that pH conditions can direct hydrogel formation and stability by mediating the coupling of Au NP (citrate reduced) ,  and the pVIII (Fig. 1). By adjusting the pH, differences between native or mutant major capsid can be offset assuring hydrogel assembly with either phage system.
Phage charge computation
Because many of the phage physical-chemical properties are defined by the structure and charge of the pVIII displayed peptides, the first step in characterizing the Au NP interaction with phage was to generate a molecular model which identified the charge distribution and structure of the native and mutant pVIII protein (Fig. 2A and B). The mutant phage were genetically modified ,  to display a peptide extension of arbitrary sequence that carried a higher positive charge character relative to the native pVIII at all pHs (Fig. 2A). The graphical outcome of these calculations (with GRASP and DeepView software) shows the positive regions of the pVIII peptide in blue, the negative domains in red, and hydrophobic regions in white (Fig. 2B).
(A) Theoretical calculation based on individual amino acid charge of the native and mutant pVIII protein as a function of pH. (B) pVIII structure generated using DeepView images of the native (top) and a mutant version (bottom) of the pVIII protein. The positively charged domains are shown in blue and negative ones are in red. Hydrophobic regions appear white. The native sequence was: NH3+-aegddpakaafdslqasateyigyawam vvvivgatigiklfkkfts-COO− and the mutant one was NH3+-PRQIKIWFQNRRMKWKKPae gddpakaafdslqasateyigyawamvvvivgatigiklfkkfts-COO− (capitalized residues and boxed region represent the mutant peptide extension).
pH dependence studies
In order to characterize and compare the interactions of Au NP with either native or mutant phage, we evaluated the dependence of several experimental observables as a function of pH. We first identified the formation of Au-phage hydrogels with either native or mutant phage (Fig. 3A, suspended gel structures with red coloration). Then, darkfield microscopy (elastic scattering, Fig. 3B) and fractal dimension (Df) analysis (Fig. 3C) was applied to quantify the differences in microstructures of the hydrogel systems (Fig. 3B). The fractal dimension (Df) of a nanoparticle assembly is a quantitative measure of their structural organization , . After this, we performed two separate pH titrations. In the first titration, we measured the Au-phage optical properties by means of Uv-vis spectroscopy (Uv-vis). When using Uv-vis, the Au NP-phage interactions (native and mutant) were detected by monitoring the shift in the plasmon resonance of the Au NP into the NIR (Fig. 4A). This red shift (indicated by the increase in 750 nm extinction) generally occurs when the distance between Au NP (dAu) is less than the average particle diameter (2rAu; dAu≤2rAu) , . In the second titration, we used surface plasmon resonance (SPR) spectroscopy, where a Au surface is used to evaluate the Au-phage interaction without the presence of Au NP , . Furthermore, the purpose of using SPR spectroscopy is to use a Au surface as a sensor and to mimic the Au NP-phage interaction (Fig. 4B).
(A) Vials with hydrogels prepared with native and mutant phage at pH 2.0 (top) and 5.5 (bottom). Au NP of 50±8 nm were prepared by citrate reduction. (B) Darkfield micrographs (elastic scattering) of hydrogels in (A) (constant light intensity). (Scale bar, 10 µm). (C) Df of structures in (B) determined with box counting Df analysis (ImageJ software).
(A) Light extinction at 750 nm for hydrogels as a function of pH. (B) SPR measurements of phage interaction with citrate-treated Au surface vs. pH (buffer background signal subtracted from data). (C) Surface charge density calculation based on individual amino acid charge present on mutant peptide extension.
Phage charge computation
The higher positive charge distribution of the mutant pVIII (Fig. 2B) is in qualitative agreement with the charge estimated from the primary sequence of the peptide extension (Fig. 2A). The assembly and stability of hydrogels is due to the interplay of ligand exchange, long- and short-range interactions. For Au-phage networks, the interactions are convoluted by the adsorbed citrate layer on the particle surface, which is oriented with the six carboxylic oxygen atoms aligned with gold atoms of a 111 surface . Chen et al. proposed that molecules containing carboxylic acid groups can displace citrate on gold surfaces through ligand exchange . The molecular model images (Fig. 2B) show that many of these acids are oriented with the carboxylic acid groups pointed outwards, which suggests that formation and stability of Au-phage assembly for the native phage is a combination of citrate replacement coupled with electrostatic interaction between the positive residues on the pVIII and Au NP. In the mutant pVIII, more positive character is available in the exposed capsid surface, which should influence the phage interaction with negatively charged Au NP as a function of pH.
pH dependence studies
All four experiments indicated a distinct pH dependence behavior between the native and mutant phage. This difference was visually detectable (Fig. 3A and B) as well as quantifiable from the Df analysis from the elastic scattering images (Fig. 3C). First, at pH 2.0 the mutant system failed to form hydrogel structures (Fig. 3A top right vial) indicated by the distinct light scattering behavior (white color instead of pink structures) and lower Df (1.50±0.07) than all other systems (Fig. 3C). Next, the pH titrations using either 750 nm extinction (with Au NP; Fig. 4A) or SPR spectroscopy (Au flat surface, absence of Au NP; Fig. 4B) measurements, underscored the assembly differences between the two systems. Both titrations showed a “threshold” behavior for the mutant system, where a sharp increase in extinction (Fig. 4A) and SPR (Fig. 4B) signal was observed for pHs below 5.0. Notably, this pH threshold (pH = 5.0) overlaps with the onset of the calculated net positive charge (pH < pI) of the mutant peptide extension (Fig. 4C and Fig. 2B, dashed box). The SPR measurements followed the same trend, with an increase in phage adsorption to the Au surface at a lower pH (pH≤5.0). At pH 2.0, the mutant phage SPR signal is twice as high (5,000 RU) as the one with the native phage (2,500 RU, Fig. 4B). This result supports the hypothesis that the predicted increase in positive charge of the mutant peptide extension as the pH is decreased (pH≤5; Fig. 4C) favors the opposite charge affinity between the phage and the Au NP. Furthermore, the increased phage adsorption observed with mutant phage system (Fig. 4B), seem to prevent hydrogel formation (Fig. 2A), indicated by the presence of the red shift in absorption from Au NP (Fig. 4A). One must emphasize that the Au NP are dispersed within the hydrogel structures (dAu>2rAu; Fig. 3A, top-left, bottom-left and bottom-right vials) , indicated by the low 750 nm extinction signals (Fig. 4A). Therefore, at pH 2.0, the high 750 nm extinction values of the mutant phage system, resulting from the shortening of the Au NP inter-particle distance, indicates an increase in Au NP density. This increased density likely contributes in preventing the formation of the water-suspended hydrogel assemblies (Fig. 3A, top right).
These results show that by tuning the pH, and therefore controlling phage surface charge, the direct-assembly of Au NP and phage can be induced into stable hydrogels in spite of the differences in the phage major capsid protein and without the need of phage display library screening. Furthermore, because of the significant structural and chemical differences in the environment in which the pIII and pVIII proteins are displayed, such pH dependence studies can provide additional insight into the interaction and assembly role of peptide motifs selected with pIII libraries within the more representative context of the pVIII environment. When considering the phage surface area (∼18,500 nm2, mostly made of pVIII) and capsid dimensions , , the location and structural environment of the minor capsid consist of 3 to 5 copies of the pIII displayed on an area (at one of the phage extremity; Fig. 1) of approximately 28 nm2, which translates to a peptide surface density of approximately 2–3 peptide/nm2. In contrast to the minor capsid, the pVIII mutant peptide extension are dispersed across the surface of the major capsid with approximately one mutant extension displayed for every 26 native copies of pVIII. Therefore, the surface frequency/density of this pVIII mutation (1 for every 200 nm2) is substantially lower than the one for the peptides displayed on the minor capsid (2–3 pIII for every 1 nm2). Thus, considering these structural differences, the assumption that pIII displayed peptides affinity to nanoparticles would be conserved when displayed on the pVIII may not always be accurate. Finally, given the challenge for reproducibly building functional structures at the nanometer scale, the streamlined methodology reported here may serve as a complementary approach to understand and to gain control of the assembly of biologically based nanoparticles with or without genetic manipulation of phage capsid. The modularity of phage and the number of possible applications for such bioinorganic hydrogels along with its versatility at various pH is a needed characteristic for the fabrication and implementation of economically relevant materials which can produce practical bio-electronic, environmental and biomedical tools.
Materials and Methods
Au-phage hydrogel assembly
The assembly of Au-phage hydrogel was achieved by adding Au NP (1.2 pM) in equal volumes to 150 µl aqueous solution of phage (native or mutant with light extinction of 0.14 a.u. at 270 nm) in aqueous solution of varying pHs (5 mM HCl pH 2, 5 mM Glycine buffer for pHs 2.5, 3.0, and 3.5, 5 mM acetate buffer for pHs 4.0 and 5.0, 5 mM boric acid for pH 5.5, 5 mM borate buffer for pH 8.5, 5 mM NaOH pH 14). Hydrogels were allowed to form overnight at room temperature. The 50±8 nm Au NP solution, verified by transmission electron microscope (TEM) image analysis, was prepared following the common citrate-reduction  procedure (molar ratio of 0.8∶1 of sodium citrate:Au(III) chloride). Au(III) chloride (99.99+%) was purchased (Sigma-Aldrich).
The Uv-vis spectroscopy measurements were performed with a plate reader spectrometer (Spectramax M5, Molecular Devices).
A Biacore 3000 was used for SPR measurements of phage adsorption onto sodium citrate (0.3 mM) treated Au surfaces (Biacore Life Scieces). Phage solutions were prepared with buffers of respective pH (listed above). After each phage adsorption measurement (20 µl/min flow rate) the Au surface was treated with 50 mM NaOH, with picopure H2O and 0.3 mM sodium citrate. Finally, the buffer background signal was subtracted from sample data for each respective condition.
Native or mutant phage were prepared by means of bacterial infection , . The mutant phage was genetically modified ,  to display a peptide extension of arbitrary sequence (Fig. 2). The peptide extension repeats were displayed once every 26 times pVIII peptides were displayed (∼104 out of 2,700 peptide total for the major capsid composition) , .
Conceived and designed the experiments: GS JM. Performed the experiments: GS JM DF JE. Analyzed the data: GS JM EY. Contributed reagents/materials/analysis tools: GS JM RR LG. Wrote the paper: RP GS JM WA. Other: Supervised the work: WA RP.
- 1. Souza GR, Christianson DR, Staquicini FI, Ozawa MG, Snyder EY, et al. (2006) Networks of Gold Nanoparticles and Bacteriophage as Biological Sensors and Cell Targeting Agents. Proc Natl Acad Sci USA 103: 1215–1220.
- 2. Leite ER (2004) Nanocrystals assembled from the bottom up. In: Nalwa HS, editor. Encyclopedia of Nanoscience and Nanotechnology. Stevenson Ranch, , CA: American Scientific Publishers. pp. 537–554.
- 3. Zacher AN III, Stock CA, Golden JW II, Smith GP (1980) A new filamentous phage cloning vector: fd-tet. Gene 9: 127–140.
- 4. Chen L, Zurita AJ, Ardelt PU, Giordano RJ, Arap W, et al. (2004) Design and validation of a bifunctional ligand display system for receptor targeting. Chem Biol 11: 1081–1091.
- 5. Barbas CF III, Burton DR, Scott JK, Silverman GJ (2001) Phage Display, A Laboratory Manual. New York: Cold Spring Harbor.
- 6. Arap W, Pasqualini R, Ruoslahti E (1998) Cancer treatment by targeted drug delivery to tumor vasculature in a mouse model. Science 279: 377–380.
- 7. Hajitou A, Trepel M, Lilley CE, Soghomonyan S, Alauddin MM, et al. (2006) A hybrid vector for ligand-directed tumor targeting and molecular imaging. Cell 125: 385–398.
- 8. Huang Y, Chiang CY, Lee SK, Gao Y, Hu EL, et al. (2005) Programmable Assembly of Nanoarchitectures Using Genetically Engineered Viruses. Nano Lett 5: 1429–1434.
- 9. Sarikaya M, Tamerler C, Jen AK, Schulten K, Baneyx F (2003) Molecular biomimetics: nanotechnology through biology. Nature Mater 2: 577–585.
- 10. Zhong Z, Patskovskyy S, Bouvrette P, Luong JHT, Gedanken A (2004) The Surface Chemistry of Au Colloids and Their Interactions with Functional Amino Acids. J Phys Chem B 108: 4046–4052.
- 11. Sigal GB, Bamdad C, Barberis A, Strominger J, Whitesides GM (1996) A self-assembled monolayer for the binding and study of histidine-tagged proteins by surface plasmon resonance. Anal Chem 68: 490–497.
- 12. Souza GR, Levin CS, Hajitou A, Pasqualini R, Arap W, et al. (2006) In Vivo Detection of Gold-Imidazole Self-Assembly Complexes: NIR-SERS Signal Reporters. Anal Chem 78: 6232–6237.
- 13. Weisbecker CS, Merritt MV, Whitesides GM (1996) Molecular self-assembly of aliphatic thiols on gold colloid. Langmuir 12: 3763–3772.
- 14. Shipway AN, Lahav M, Gabai R, Willner I (2000) Investigations into the electrostatically induced aggragation of Au nanoparticles. Langmuir 16: 8789–8795.
- 15. Chen C, Daniel MC, Quinkert ZT, De M, Stein B, et al. (2006) Nanoparticle-Templated Assembly of Viral Protein Cages. Nano Lett 6: 611–615.
- 16. Souza GR, Miller JH (2006) Elastic Light Scattering of Biopolymer/Gold Nanoparticles Fractal Aggregates. In: Geddes C, editor. Annual Reviews in Plasmonics. New York: Kluwer Academic/Plenum Publishers.
- 17. Souza GR, Miller JH (2001) Oligonucleotide detection using angle-dependent light scattering and fractal dimension analysis of gold-DNA aggregates. J Am Chem Soc 123: 6734–6735.
- 18. Peterson AW, Wolf LK, Georgiadis RM (2002) Hybridization of mismatched or partially matched DNA at surfaces. J Am Chem Soc 124: 14601–14607.
- 19. Lin Y, Pan GB, Su GJ, Fang XH, Wan LJ, et al. (2003) Study of Citrate Adsorbed on the Au(111) Surface by Scanning Probe Microscopy. Langmuir 19: 10000–10003.
- 20. Handley DA (1989) Methods for synthesis of colloidal gold. In: Hayat MA, editor. Colloidal Gold: Principles, Methods, and Applications. San Diego: Academic Press. pp. 23–27.